THE TRIBOLOGICAL PROPERTIES OF COATINGS LUBRICATED WITH A BIODEGRADABLE CUTTING FLUID
Journal Title: Tribologia - Year 2015, Vol 263, Issue 5
Abstract
This paper presents the tribological results of on investigations of TiAlN coatings that were deposited on HS6-5-2C steel using the physical vapour deposition PVD technique. An observation of the coating structure was carried out using a scanning electron microscope SEM JSM - 7100F. Examinations of the geometric structures of the surface TiAlN coating before and after tribological tests were performed using an optical profilometer Talysurf CCI Lite. The tribological tests were performed using a T-01 M tester working in a ball-on-disk combination in sliding movement. Tests were carried out under friction with lubrication using cutting fluid containing improved additive-zinc aspartate. Studies have shown that the cutting fluid influenced the formation of anti-wear surface layers, which are secured against the direct contact of rubbing surfaces. This had the effect of reducing the resistance movement and, in addition, provided protection against corrosion during tests.<br/><br/>
Authors and Affiliations
Joanna KOWALCZYK, Monika MADEJ, Dariusz OZIMINA
Keywords
Related Articles
- EP ID EP255869
- DOI -
- Views 52
- Downloads 0
TEM OBSERVATIONS OF THE WEAR OF Ti/TiN MULTILAYER COATINGS AFTER BALL-ON-DISC TEST
The wear mechanisms of single- layered TiN coatings as well as multilayered Ti/TiN coatings (Λ =250nm) were investigated with ball-on-disc test. The coatings were obtained by the hybrid pulsed laser deposition (PLD) tech...
Skutki eksploatacyjne smarowania silnika spalinowego preparatem eksploatacyjnym o działaniu chemicznym
W opracowaniu przedstawiono wyniki badań zmian w procesie eksploatacji własności oleju silnikowego CE/SF SAE 15W/40 oraz modyfikowanego preparatem eksploatacyjnym o działaniu chemicznym Motor Life Professional. Badania o...
DOŚWIADCZALNA OCENA DOPUSZCZALNYCH WARUNKÓW EKSPLOATACJI DLA ŚLIZGOWEGO SKOJARZENIA DLC/STAL
Przedstawiono przebieg i wyniki badań tarcia ślizgowego skojarzenia próbek ze stali wysokostopowej z powłoką DLC do zastosowań przemysłowych naniesioną na jedną ze stron skojarzenia. Badania stanowiły część prac związany...
THE TRIBOLOGICAL PROPERTIES OF METAL-POLYMER COMPOSITES IN DRY CONDITIONS
In the paper, the results of tribological tests of metal-polymer composites and bronze pair without external lubrication were presented. The friction and wear tests were performed using the composites with solid lubrican...
Warstwa graniczna w procesie tarcia
Zwiększają się względne prędkości współpracujących elementów maszyn i przenoszone przez nie obciążenia, przy wyraźnej tendencji do zmniejszania ich ciężaru. Wobec tego coraz większego znaczenia nabierają problemy jakości...