Analysis of the Nucleation Activity of Wood Fillers for Green Polymer Composites

Journal Title: Fibres and Textiles in Eastern Europe - Year 2018, Vol 26, Issue 2

Abstract

In this work, the surface of pine wood used as a filler in polypropylene/wood composites was successfully modified by the mercerization process. It is a very significant process because it removes low-molecular components, which improves interactions between the filler and matrix and leads to a better dispersion of the filler in the matrix. Unfortunately chemical treatment may affect nucleation of the lignocellulosic filler. On the basis of XRD results, the transformation of native cellulose I to cellulose II was observed. In the present study, the effect of the mercerisation of pine wood on the nucleation ability of polypropylene was investigated by means of polarising microscopy. The results showed that the chemical modification of pine wood had a significant effect on nucleation activity in polymer composites. This effect is explained by differences in the chemical compositions of wood fibres. The content of simple sugars obtained from the methanolysis and acidic hydrolysis of cellulose and hemicellulose was determined through gas chromatography investigations. It was found for the first time that the formation of transcrystalline structures is possible for composites with a high content of glucose derived from cellulose. It is also worth emphasising that the chemical modification process can lead to cellulose depolymerisation processes and the formation of degradation products with a lower molecular weight. Knowledge of the phenomena taking place in the interphase boundary polymer/ filler is very important because it permits optimisation of the processing, leading to products of target properties.<br/><br/>

Authors and Affiliations

Majka Odalanowska, Sławomir Borysiak

Keywords

Related Articles

Określanie szorstkości powierzchni tkanin przy zastosowaniu techniki projekcji nierówności typu Moiré

W pracy zaproponowano nową metodę charakteryzacji szorstkości powierzchni tkanin. Jest ona oparta na projekcji zagnieceń techniką Moiré i analizy otrzymanych wzorów uzyskanych poprzez interakcje pomiędzy siatką Ronchiego...

Cotton Fibre-to-Yarn Engineering: A Simulated Annealing Approach

In this paper we undertake to engineer yarn of predefined strength by choosing suitable raw material and process parameters. In an attempt to achieve a yarn of optimal strength, the constrained optimisation problem is fo...

Lithuania, Kaunas, Textile Institute, SRI Center for Physical Sciences and Technology

Eco-friendly textile biocomposites with PLA matrix reinforced with flax and flax/PLA weft knitted fabrics without any additional chemical treatment were prepared in this study. Five different kinds of samples were manufa...

Wpływ postawy ciała mężczyzny i jego kształtu na projektowanie i dopasowanie ubioru

W pracy zaprezentowano badania wpływu postawy ciała i występowania funkcjonalnych i strukturalnych zmian ciała na dopasowanie ubioru. Przeprowadzano skanowanie 3D próby składającej się z 50 męskich osobników. Określono i...

Wpływ użytkowania ręcznie wiązanych dywanów na ich odporność przy ściskaniu

Właściwości podczas ściskania są podstawowym czynnikiem określającym żywotność każdego dywanu. Odporność na ściskanie okrywy dywanu, jako jedna z podstawowych właściwości ściskania dywanu zmienia się z ich ekspozycją na...

Download PDF file
  • EP ID EP270037
  • DOI 10.5604/01.3001.0011.5741
  • Views 70
  • Downloads 0

How To Cite

Majka Odalanowska, Sławomir Borysiak (2018). Analysis of the Nucleation Activity of Wood Fillers for Green Polymer Composites. Fibres and Textiles in Eastern Europe, 26(2), 66-72. https://europub.co.uk./articles/-A-270037