Comparative Study of Shear Bond Strength of Three Veneering Ceramics to a Zirconia Core
Journal Title: Journal of Dental Biomaterials - Year 2016, Vol 3, Issue 1
Abstract
Statement of Problem: Fracture of veneering porcelain has been described as the most frequent reason for the failure of zirconia-based fixed restorations. Objectives: The purpose of this study was to evaluate and compare the shear bond strength of a zirconium oxide core material to three commercial veneering ceramics. Materials and Methods: Three types of veneering ceramics were selected including IPS -emax Ceram, Vita VM9, and Cerabien. Thirty block specimens of zirconia core material were prepared in 4×4×9 mm dimensions. Three groups were created and the veneering ceramic was added to each of 10 blocks. Shear bond test was conducted with universal testing machine. Data were analyzed using one-way ANOVA (p = 0.05). Results: Mean shear bond strength values and standard deviations were 26.03 MPa (6.32), 23.85 MPa (4.01), and 19.16 MPa (3.72) for Vita VM9, IPS emax Ceram, and Cerabien, respectively. Cerabien ceramic showed more failure as compared to the other ceramics. However, there was no significant difference among the three veneering groups. Conclusions: Within the limitation of this study, it can be concluded that shear bond strength between zirconia core and three veneering ceramics was not significantly different.
Authors and Affiliations
Sh Aalaei, F Nematollahi, M Vartanian, E Beyabanaki
Keywords
Related Articles
- EP ID EP248716
- DOI -
- Views 68
- Downloads 0
Combination Effect of Hemostatic and Disinfecting Agents on Micro-leakage of Restorations Bonded with Different Bonding Systems
Statement of Problem: Hemostatic agents may affect the micro-leakage of different adhesive systems. Also, chlorhexidine has shown positive effects on micro-leakage. However, their interaction effect has not been reported...
The Effect of Pre-heating Silorane-based Composite Resin on Marginal Gap Formation of Class V Restorations
Statement of problem: Many efforts have been made to solve the problem of composite resin adaptation and reduce microleakage. Objective: The aim of the present study was to evaluate the effect of preheating of silorane-b...
The Effect of Drinks and Temperature on the Staining of Resin Composites Coated with Surface Sealants
Statement of problem: Surface staining of resin composite by dietary factors may be modified by the placement of a low-viscosity surface sealant aimed at reducing surface voids and defects occurring after light-curing an...
Marginal Micro-leakage of Self-etch and All-in One Adhesives to Primary Teeth, with Mechanical or Chemo-Mechanical Caries Removal
Statement of Problem: Chemo-mechanical caries removal is an effective alternative to the traditional rotary drilling method. One of the factors that can influence micro-leakage is the method of caries removal. Objectives...
Hertzian Load-bearing Capacity of Hybrid and Nano-hybrid ResinComposites Stored Dry and Wet
Statement of Problem: Hertzian indentation test has been proven to be an efficient and reliable alternative upon Vickers hardness test. This method has been used to test dental ceramics, amalgams, glass ionomers and luti...