Control of cast iron and casts manufacturing by Inmold method
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 3
Abstract
In this paper the usability of cast iron spheroidizing process in mould control by ATD method as well as by ultrasonic method were presented. Structure of instrumentation needed for control form performance of cast iron spheroidizing by Inmold method was illustrated. Author, pointed out that amount of magnesium master alloy should obtain 0,8 ÷ 1,0% of mass in form at all. Such quantity of preliminary alloy assure of obtain of nodular graphite in cast iron. In consequence of this, is reduce the cast iron liquidus temperature and decrease of recalescence temperature of graphite-eutectic crystallization in compare with initial cast iron. Control of casts can be carried out by ultrasonic method. In plain cast iron, ferritic-pearlitic microstructure is obtaining. Additives of 1,5% Cu ensure pearlitic structure.
Authors and Affiliations
S. Pietrowski
Keywords
Related Articles
- EP ID EP72022
- DOI -
- Views 97
- Downloads 0
Tribological resistance of high speed steel HS 6-5-2 remelted with electric arc
The intensity of tribological wear of the high speed steel HS 6-5-2 remelted with the GTAW method has been compared to the heat treatment steel in a conventional way. Moreover, the types of the wear appeared during the f...
Influence of water-glass grade and quantity on residual strength of microwave-hardened moulding sands. Part 2
The paper continues dealing with the issues of influence of microwave hardening on mechanical properties of waterglass-based moulding sands. This second part of the research includes examining moulding sands containing 1...
Influence of heat treatment on microstructure and properties of GX12CrMoVNbN9-1 cast steel
The paper presents results of research on the influence of multistage heat treatment on microstructure and properties of high-chromium martensitic GX12CrMoVNbN9 – 1 (GP91) steel. The material under investigation were sam...
Stereology of carbide phase in modified hypereutectic chromium cast iron
In paper are presented results of studies of carbide phase stereology modified hypereutectic wear resistance chromium cast iron which contains carbon about 3,5% and chromium about 25%. Three substances were applied to th...
Effect of thickness of refractory coating on the Lost Foam Process
The analysis of the influence of the thickness of refractory coating on the production process of casts in the Lost Foam process was introduced in the work. It was conducted in the peculiarity the analysis simulating inv...