Copper infiltrated high speed steel skeletons
Journal Title: Archives of Materials Science and Engineering - Year 2019, Vol 1, Issue 98
Abstract
Purpose: This article is a monographic summary of the most important research results from the last 10 years regarding HSS based materials. This materias were produced with powder metallurgy technology using spontaneous infiltration. The presented results answer the question of how iron, tungsten carbide and copper additives influence the final properties of these materials and present additional microstructural phenomena revealed during their manufacture. Design/methodology/approach: Materials were produced by spontaneous infiltration. Porous skeletons for infiltration were produced by pressing and pressing and sintering of mixed powders. Copper was used as the infiltrant. Findings: The molten copper was drawn into the porous skeletons, through a capillary action, and filled virtually the entire pore volume to get the final densities exceeding 97% of the theoretical value. Research limitations/implications: As part of further research, microstructures of M30WC composites obtained by direct infiltration of copper into as-sintered porous skeletons using TEM are planned. Practical implications: Efficiant mechanical strength, high hardness, adequate heat resistance and good wear resistance of M3 type 2 HSS powder produced by woter atomisation make it an attractive material for manufacture of valve train components, for example valve seat inserts. Originality/value: The novelty in the article are the results of research on the microstructure made using TEM, the results of testing materials after heat treatment, untypical for high- speed steels. The article attempts to explain the influence of iron addition on properties - such a slight loss of mass as a result of its addition. The second aim of this work is to analyse the microstructural changes during sintering porous skeletons made from HSS with WC additions.<br/><br/>
Authors and Affiliations
M. Madej
Keywords
Related Articles
- EP ID EP640870
- DOI 10.5604/01.3001.0013.3391
- Views 68
- Downloads 0
Characteristic of MAO coatings formed on CuAl2 in-situ reinforced Aluminum Matrix Composites
Purpose: The aim of this study was to examine the structural and mechanical properties of coatings formed on CuAl2 in-situ reinforced aluminium matrix composites (AMCs) by micro arc oxidation (MAO) process...
Combined thermal, microstructural and microchemical analysis of solidification of Al25Si3Cu alloy
Purpose: This paper present thermal and microstructural and microchemical analyses were conducted on the unmodified experimental alloy Al20Si3Cu (B390.1) solidified in the High Temperature Universal Metallurgical Simulat...
Microstructure and mechanical properties of the annealed 6060 aluminium alloy processed by ECAP method
Purpose: The main goal of this paper is to present the investigation results of microstructuralevolution and mechanical properties changes in commercial EN AW 6060) aluminium alloyafter intensive plastic deformation, obt...
Devices for modern vacuum heat treatment
Purpose: A review regarding the devices for vacuum heat treatment is presented. Design/methodology/approach: Devices for modern heat treatment has been reviewed. The devices has been classified regarding the heat treatme...
Preparation and investigations of electrical and optical properties of thin composite layers PAN/SiO2, TiO2 and Bi2O3
Purpose: The aim of this study was to present the influence of mass concentration of the reinforcement phase on the structure and optical properties of the obtained composite thin films with a polymer matrix reinforced b...