Effect of Combined Calcium Hydroxide and Accelerated Portland Cement on Bone Formation and Soft Tissue Healing in Dog Bone Lesions
Journal Title: Journal of Dental Biomaterials - Year 2015, Vol 2, Issue 3
Abstract
Statement of Problem: Recent literatures show that accelerated Portland cement (APC) and calcium hydroxide Ca (OH)2 may have the potential to promote the bone regeneration. However, certain clinical studies reveal consistency of Ca (OH)2, as one of the practical drawbacks of the material when used alone. To overcome such inconvenience, the combination of the Ca (OH)2 with a bone replacement material could offer a convenient solution. Objectives: To evaluate the soft tissue healing and bone regeneration in the periodontal intrabony osseous defects using accelerated Portland cement (APC) in combination with calcium hydroxide Ca (OH)2, as a filling material. Materials and Methods: Five healthy adult mongrel dogs aged 2-3 years old (approximately 20 kg in weight) with intact dentition and healthy periodontium were selected for this study. Two one-wall defects in both mesial and distal aspects of the 3rd premolars of both sides of the mandible were created. Therefore, four defects were prepared in each dog. Three defects in each dog were randomly filled with one of the following materials: APC alone, APC mixed with Ca (OH)2, and Ca (OH)2 alone. The fourth defect was left empty (control). Upon clinical examination of the sutured sites, the amount of dehiscence from the adjacent tooth was measured after two and eight weeks, using a periodontal probe mesiodistally. For histometric analysis, the degree of new bone formation was estimated at the end of the eighth postoperative week, by a differential point-counting method. The percentage of the defect volume occupied by new osteoid or trabecular bone was recorded. Results: Measurement of wound dehiscence during the second week revealed that all five APCs had an exposure of 1-2 mm and at the end of the study all samples showed 3-4 mm exposure across the surface of the graft material, whereas the Ca (OH)2, control, and APC + Ca (OH)2 groups did not show any exposure at the end of the eighth week of the study. The most amount of bone formation was observed in APC group which was significantly different with all other groups (p < 0.05). Conclusions: Despite acceptable soft tissue response of Ca (OH)2 , this additive material could not be suggested because of negative effects on bone formation results.
Authors and Affiliations
H Khorshidi, S Raoofi, Z Behboud, Gh Mozafari, MJ Ashraf
Keywords
Related Articles
- EP ID EP248922
- DOI -
- Views 91
- Downloads 0
Recent Advances and Future Perspectives for Reinforcement of Poly(methyl methacrylate) Denture Base Materials: A Literature Review
Poly(methyl methacrylate) (PMMA) is the most common material used to fabricate complete and partial dentures. Despite its desirable properties, it cannot fulfill all mechanical requirements of prosthesis. Flexural fatigu...
Comparison of Bone Biomechanical Behavior around Three Different Mini-Implant Systems Employing Finite Element Method
Statement of Problem: Placement of mini-dental implants when single-tooth restorations are needed and the space is not sufficient to insert a standard diameter implant is indicated. There are many different mini-implant...
Impacted Mandibular Third Molar, Associated Pathoses, and Their Relation to Angulation and Impaction Depth: A Cone Beam CT Study
Statement of problem: prophylactic removal of the impacted lower third molar (ILTM) is controversial and accompanying pathologic conditions play an important role. Objectives: The aim of the present study is to evaluate...
The Effect of Pre-heating Silorane-based Composite Resin on Marginal Gap Formation of Class V Restorations
Statement of problem: Many efforts have been made to solve the problem of composite resin adaptation and reduce microleakage. Objective: The aim of the present study was to evaluate the effect of preheating of silorane-b...
Vickers Hardness of Composite Resins Cured with LED and QTH Units
Statement of Problem: One of the factors affecting the degree of polymerization of light-cured composites is the type of light-curing unit used. In addition, physicomechanical properties of the composite resins depend on...