Effect of Friction in the Punch-to-Specimen Contact Zone Upon the Punching Behaviour of Synthetic Leathers
Journal Title: Fibres and Textiles in Eastern Europe - Year 2017, Vol 25, Issue 3
Abstract
Upholstery materials during their performance experience biaxial deformations, which are effected by friction in the contact zones: material-to-human skin, material-to-material, and material-to-inner parts of the furniture. The aim of this research was to define the effect of friction in the punch-to-specimen contact zone upon the tearing character and strength of non-perforated and perforated synthetic leathers under biaxial punching. Tests were performed with three different punches. The variation of friction coefficients in the punch-to-leather contact zone was achieved by the application of four different lubricants. Leather samples were investigated on the face (vinyl) and reverse (textile) sides. The results of the investigations confirmed that the maximal punching force Pmax increases with an increase in the punch size. The same tendency is valid in cases where different levels of friction act in the punch-to-specimen contact zone or whether the specimens were punched from both sides. Dependencies exist between area S of the punch-to-specimen contact zone during tearing and the average static μSA and dynamic μDA friction coefficients.
Authors and Affiliations
Donata Zubauskienė, Eugenija Strazdiené
Keywords
Related Articles
- EP ID EP199544
- DOI 10.5604/01.3001.0010.1700
- Views 78
- Downloads 0
Badanie przepływu ciepła wywołanego promieniowaniem przez aluminiowane wielowarstwowe tkaniny przy niskim poziomie termicznego promieniowania
Przedstawiono metodę pomiaru strumienia ciepła wywołanego promieniowaniem przechodzącym przez aluminiowane wielowarstwowe tkaniny ubrań ochronnych. Wyniki wykazały, że przy wzroście grubości tkaniny z włókna szklanego, t...
Effects of the Laundering Process on Dimensional and Physical Properties of Plain and Lacoste Fabrics Made from Modal/combed Cotton Blended Yarns
In this study, dimensional and some physical properties of plain (single jersey) and lacoste knitted fabrics made from 50/50 modal/combed cotton blended yarns (tex 21 and 15) were investigated. Twelve weft knitted fabric...
Flexural Behaviour of Fibre Reinforced Concrete Beams with Different Aspect Ratios
The performance of conventional concrete is enhanced by the addition of fibres in concrete. Consequently the brittleness in concrete is reduced, and its acceptable ductility is also ensured by this addition. In this pape...
Research of Fluorinated Acrylate Copolymer on Flax Fabric
A fluorine-containing acrylate copolymer emulsion was prepared in this study, which was applied to finishing linen fabric. Dodecafluloroheptry methacrylate (G04) was used as a modified monomer, butylacrylate (BA) and met...
Badania porównawcze właściwości przędz Vortex i obrączkowych oraz właściwości tkanin zawierających te przędze w wątku
Wybrano dwie różne mieszanki włókien (bawełna PET i PA6.6) w różnych proporcjach, jak również jednorodne włókna celulozowe typu Modal. Wyprodukowano przędze Vortex i obrączkowe o masie liniowej 16 tex i 67 tex. Badania w...