Efficiency of protective coatings on high creep resistant cast steel
Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
This paper presents results of research of multilayer aluminium–silicon coatings. Aluminium–silicon coatings were created on high– temperature creep resist cast iron using slurry method in air atmosphere. These coatings protect equipment against hot corrosion in carburizing atmosphere at thermal shocks conditions. Various technological parameters of coatings manufacturing were applied. Main technological parameters were: temperature and time of annealing and Al-Si ratio in the active mixture. The structure of obtained coatings is three-zonal. Phase composition of two external zones ensures protection against carburizing, but these zones are not resistant to cracking. The cracks form as a result of thermal shocks. The internal zone of the coatings situated next to substrate compensates for differences of thermal expansion of the coating and the substrate. The cracks are stopped in the internal zone and do not propagate into the substrate material. Protective efficiency of the coatings at carburizing conditions with thermal shocks was determined. Structure of the coatings before and after carburizing and thermal shocks is described in present paper. Thickness, chemical composition (EDS) and phase composition (XRD) of the coatings are determined. Correlation between the coatings structure and depth of carburized layer was determined.
Authors and Affiliations
A. Kochmańska, J. Kubicki
Keywords
Related Articles
- EP ID EP70558
- DOI -
- Views 95
- Downloads 0
Effect of applied pressure on the quality of squeeze cast parts made from AlSi9Mg alloy
The results of the study of an influence of pressure in the direct squeeze casting process on the physical and mechanical properties of an AlSi9Mg alloy are presented. The specimens were made by casting the tested AlSi9M...
Compensation of reactive power in the power-supplying system in a roller mixer in laboratory conditions
Of particular importance are instantaneous voltage and current levels registered in the three-phase power-supplying systems in roller mixer in laboratory conditions. Recorded data allow the apparent power, active and rea...
Analysis of the Inconel 600 alloy destruction process in the surrounding of oxygen, nitrogen and hydrogen
This paper presents results of research, which was targeted to define reasons of the short life of sieves made from a 0.8mm diameter wire of the INCONEL 600 alloy. It was noticed that when the sieves were used in the dev...
Plasticity of the AlSi9Mg alloy modified with Na, F and Cl compounds
This paper presents the results of an experiment investigating the structure and the percent elongation of an AlSi9Mg alloy modified with NaCl, Na3AlF6 and NaF compounds. The alloy was modified in a crucible. The experim...
The dimensional and shape accuracy of vacuum castings prepared in plaster moulds
The results of laboratory test on the dimensional and shape accuracy of bronze plaster castings CuSn10, CuSn5Zn5Pb5and AlSi11 silumin are presented in this paper. The test castings were made in form of rods of length 100...