Evaluation of fractures in MAR-M509 alloy samples after fatigue strength tests
Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 3
Abstract
The paper presents the result of fracture analysis in MAR-M509 samples after high-cycle bending fatigue strength tests. Microstructural tests were carried out with a scanning electron microscope. To identify carbide phases a quantitative analysis of the chemical composition was made. The fracture surface and the surface in a plane perpendicular to the fracture surface were observed. It was discovered that the crack initiation and propagation occurs on carbide separations.
Authors and Affiliations
M. Mróz, W. Orłowicz
Keywords
Related Articles
- EP ID EP72149
- DOI -
- Views 99
- Downloads 0
Elements of the efficiency system improvement of foundry
The effectiveness of industrial systems is being ranked among important factors industrial engineering in foundry. He determines internal production abilities of foundry. It is possible to describe the effectiveness the...
Laboratory grey cast iron continuous casting line with electromagnetic forced convection support
The article describes the construction of a 20 mm diameter grey cast iron ingots continuous casting laboratory line. This line is made of three main units: melting unit (induction furnace), casting unit and the pulling u...
Semi-solid processing method for cast iron
A device for the fabrication of ingots from cast iron of globular non-dendritic structure of the primary phase was designed and made, using the principle of overflow on the Slope Cooling Plate, known as the SCP method....
Bell founding – the past and the present
This paper outlines the history of bell founding. The exceptional character of bells, which are products of supracultural importance, was stressed. The complexity of the bell manufacturing process and a unique approach t...
Application of Differential Scanning Calorimetry (DSC) in study of phase transformations in ductile iron
The effect of heating rate on phase transformations to austenite range in ductile iron of the EN-GJS-450-10 grade was investigated. For studies of phase transformations, the technique of differential scanning calorimetry...