Evaluation of properties of plywood glued with composite adhesive based on waste paper, PEG and PF resin
Journal Title: Annals of WULS, Forestry and Wood Technology; Zeszyty naukowe SGGW - Year 2017, Vol 99, Issue
Abstract
Evaluation of properties of plywood glued with composite adhesive based on waste paper, PEG and PF resin. The study developed a method for manufacturing a new adhesive mixture involving different amounts of an industrial PF resin and a biocomposite adhesive based on waste paper and PEG 600. During the research, formulations and basic properties of the mixtures were determined, and then the mixtures were used to produce experimental plywood, for which the bonding quality was determined using tests required by PN-EN 314-2. The study showed that an increase in PF resin substitution rate resulted in reduction in its reactivity and pH. At 40% substitution, the gel time and pH of the adhesive mixture did not differ significantly from values determined for the pure PF resin. The results of bonding quality tests for the experimental plywood showed that plywoods glued with the adhesive mixture containing 30% of the biocomposite adhesive fully met requirements for the shear strength specified in PN-EN 314-2.
Authors and Affiliations
Jakub Brózdowski, Dorota Dukarska
Keywords
Related Articles
- EP ID EP349740
- DOI -
- Views 85
- Downloads 0
Screw withdrawal capacity in wood-HDPE composites exposed to high temperature
Screw withdrawal capacity in wood-HDPE composites exposed to high temperature. The results of tests on the withdrawal capacity of screw fasteners commonly used in the wood industry and embedded in woodpolymer composites...
The state of degradation of waterlogged wood from different environments
The state of degradation of waterlogged wood from different environments The archaeological waterlogged 10th century oak wood from the Gęgnowskie Lake, as well as 11th century alder wood from Rawka river, are valuable hi...
On automated deformation measurements of timber-concrete structures
On automated deformation measurements of timber-concrete structures. For many years a dynamic development of timber structures has been observed. This fact can be explained by many factors, among others, by the developme...
Bending strength (modulus of rupture) and modulus of elasticity of MDF different density at various temperature
Bending strength (modulus of rupture) and modulus of elasticity of MDF different density at various temperature Bending strength and modulus of elasticity of MDF with thickness 10 and 16 mm and density 770…870 kg/m3 were...
Геометрия износа сверла во время обработки древесно-стружечных ламинированных плит.
Геометрия износа сверла во время обработки древесно-стружечных ламинированных плит.В данной статье рассматривается возможность использования стандартного параметра износа стальных сверл используемых в металлобработке для...