Journal Title: Archiwum Odlewnictwa - Year 2009, Vol 9, Issue 2
Abstract
In this study, a new SHSF (Self-Propagating High-Temperature Synthesis in Mould) process of synthesis of the functionally gradient materials (FGMs) was described. The said method enabled generating a thin, sub-surface layer of the MMC type in two alloys, i.e. in cast iron/NbC and Ni3Al/NbC systems. The layer was composed of fine-dispersed niobium carbides present in high volume content. The cast iron/NbC and Ni3Al/NbC materials fabricated by the SHSF process were next subjected to metallographic and structural examinations, combined with testing of mechanical properties.
Authors and Affiliations
E. Fraś, A. Janas
Keywords
Related Articles
- EP ID EP71719
- DOI -
- Views 122
- Downloads 0
Effect of applied pressure on the quality of squeeze cast parts made from AlSi9Mg alloy
The results of the study of an influence of pressure in the direct squeeze casting process on the physical and mechanical properties of an AlSi9Mg alloy are presented. The specimens were made by casting the tested AlSi9M...
Casting Ductile Iron in Layer Moulds Made from Ecological Sands
The article contains the results of tests performed under the target project in Hardtop Foundry Charsznica. The objective of the tests and studies was to develop a technology of making high-quality ductile iron castings,...
Assessment Criteria of Bentonite Binding Properties
The criteria, with which one should be guided at the assessment of the binding properties of bentonites used for moulding sands, are proposed in the paper. Apart from the standard parameter which is the active bentonite...
Influence of the technology of melting and inoculation preliminary alloy AlBe5 on change of concentration of Al and microstructure of the bronze CuAl10Ni5Fe4
Examining was the aim of the work: influence of the permanent temperature 1300°C ± 15°C and changing time of isothermal holding in the range 0÷50 minutes on the melting loss of aluminum in the bronze CuAl10Ni5Fe4; the qu...
Effect of T6 heat treatment on tensile strength of EN AB-48000 alloy modified with strontium
Among alloys of non-ferrous metals, aluminum alloys have found their broadest application in foundry industry. Silumins are widely used in automotive, aviation and shipbuilding industries; as having specific gravity near...