Genotoxicity of antibacterial bioglasses obtained by sol-gel method for Salmonella typhimurium
Journal Title: Engineering of Biomaterials / Inżynieria Biomateriałów - Year 2016, Vol 19, Issue 135
Abstract
Periodontal disease causes problems in dentistry. Surgical intervention with appropriate biomaterials for tissue regeneration is necessary in advanced stages of the disease. Therefore, the aim of this study was to determine the genotoxicity of potential biomaterials in the form of aluminosilicate bioglass (B-I) and calciumsilicate bioglasses (Z-5 and Z-8) for Salmonella typhimurium TA 98 and TA 100 in the microplate reverse mutation test. The bioglasses were extracted with 10 cm3 of dimethyl sulfoxide (DMSO), shaken at 250 rpm for 2 g of B-I and Z-8 bioglass and 1 g of Z-5 bioglass for 72 h at 37°C. Extracts of bioglasses were introduced to the test in the form of solutions in DMSO. They were partially diluted, so that during the exposure 0.25-8.0 mg/cm3 dose of B-I and Z-8 bioglasses and 0.125-8.0 mg/cm3 dose of Z-5 bioglass were obtained. Tests were carried out with and without metabolic activation at 30% of S9 fraction. B-I bioglass caused a reversion of mutations in the TA 100 strain in the presence of S9 fraction. This suggests that indirect mutagens occurred in B-I bioglass that cause base substitution mutations, which TA100 strain detect. Literature data suggests that this could be a consequence of the combined effect of the components of this bioglass and the remains of the substrates used to produce them. Z-5 and Z-8 bioglasses did not result in the reversion of the mutation against any of the test strains used. The results indicate that there should be further study of Z-5 and Z-8 bioglasses prior to their clinical application, and that B-I bioglass should not be used in the surgical treatment of periodontal disease.
Authors and Affiliations
P. Jadczyk, B. Umińska-Wasiluk, L. Ciołek, J. Karaś, A. Olszyna
Keywords
Related Articles
- EP ID EP559638
- DOI -
- Views 58
- Downloads 0
Wpływ dodatku kwasów karboksylowych na czas wiązania i wytrzymałość na ściskanie cementów szkło-jonomerowych
Cementy szkło-jonomerowe powstają w czasie utwardzania kompozycji złożonych z dwóch składników: szklanego proszku i płynu wiążącego będącego wodnym roztworem polikwasów alkenowych. Wiązanie cementu polega na reakcji kwas...
Graphene oxide and green-synthesized reduced graphene oxide in chitosanbased nanocomposites
The first part of the paper concerns synthesis and characterization of two types of nanomaterials: graphene oxide (GO) prepared by modified Marcano method and reduced graphene oxide (rGO) synthesized using green reductan...
Hydrolytic degradation of biodegradable scaffolds based on L-lactide/ glycolide/TMC and L-lactide/ glycolide/ε-caprolactone terpolymers
The main aim of this work was to check the degradation course of polymeric scaffolds in medium with and without of enzyme - pancreatic lipase. Based on the conducted degradation studies the usefulness of the formed scaff...
Evaluation of Candida albicans adhesion on AlSl-316L and Ti6Al4V in changing environmental conditions
Currently, studies on the formation of microbiological biofilm on biomaterial surfaces and medical devices have become an important aspect in medicine. In vivo studies of the biofilm development show a high correlation b...
Material and corrosion studies of conventional Co-Cr-Mo-W alloys for frame construction casts in dental prosthetics
The basic characteristics of skeletal prosthetic materials used in dentistry are: biotolerance with tissues and body fluids, as well as high pitting and crevice corrosion resistance. Also important are such characteristi...