Histomorphometric Analysis of Periodontal Tissue Regeneration by the Use of High Density Polytetrafluoroethylen Membrane in Grade II Furcation Defects of Dogs
Journal Title: Journal of Dental Biomaterials - Year 2015, Vol 2, Issue 3
Abstract
Statement of Problem: There are limited histomorphometric studies on biologic efficacy of high density tetrafluoroethylen (d-PTFE) membrane. Objectives: To investigate the healing of surgically induced grade II furcation defects in dogs following the use of dense polytetrafluoroethylene as the barrier membrane and to compare the results with the contra lateral control teeth without the application of any membrane. Materials andMethods: Mandibular and maxillary 3rd premolar teeth of 18 young adult male mongrel dogs were used for the experiment. The furcation defects were created during the surgery. 5 weeks later, regenerative surgery was performed. The third premolar teeth were assigned randomly to control and test groups. In the test group, after a full thickness flap reflection, the d-PTFE membrane was placed over furcation defects. In the control group, no membrane was placed over the defect. 37 tissue blocks containing the teeth and surrounding hard and soft tissues were obtained three months post-regenerative surgery. The specimens were demineralized, serially sectioned, mounted and stained with Hematoxylin and Eosin staining technique. From each tissue block, 35-45 sections of 10 μm thickness within 60μm interval captured the entire surgically created defect. The histological images were transferred to computer and then the linear measurement ranges of the defects area, interadicular alveolar bone, epithelial attachment and coronal extension of the new cementum were done. Then, the volume and area of aforementioned parameters were calculated considering the thickness and interval of the sections. To compare the parameters between the control and test teeth, we calculated the amount of each one proportionally to the original amount of defects. Results: The mean interradicular root surface areas of original defects covered with new cementum was 74.46% and 29.59% for the membrane and control defects, respectively (p < 0.0001). Corresponding values for epithelial attachment were 16.03% and 48.93% for the membrane and control defects, respectively (p < 0.005). The mean volume of the new bone formed in the inter-radicular defects was 61.80% and 35.93% for the membrane and control defects, respectively (p < 0.02). Conclusions: The present study provided a biological rationale for high density polytetrafluoroethylen (d-PTFE, n-PTFE) as a barrier membrane for enhancement of the bone and cementum regeneration in grade II furcation defects subjected to regeneration therapy.
Authors and Affiliations
S Raoofi, MR Shabahangfar, Gh Mozafari, M GhoraishiAbhari
Keywords
Related Articles
- EP ID EP248924
- DOI -
- Views 71
- Downloads 0
Colour Stability of Various Types of Acrylic Teeth Exposed to Coffee, Tea and Cola
Statement of Problem: Acrylic teeth of dentures are prone to discoloration due to frequent exposure to different colouring solutions in the oral environment. Thus, in order to maintain their aesthetic appearance, they mu...
Comparison of Wear Resistance of Hawley and Vacuum Formed Retainers: An in-vitro Study
Statement of Problem: As a physical property, wear resistance of the materials used in the fabrication of orthodontic retainers play a significant role in the stability and long term use of the appliances. Objectives: To...
The Effect of Bulk Depth and Irradiation Time on the Surface Hardness and Degree of Cure of Bulk-Fill Composites
Statement of Problem: For many years, application of the composite restoration with a thickness less than 2 mm for achieving the minimum polymerization contraction and stress has been accepted as a principle. But through...
Evaluation of Surface Microhardness of Silver and Zirconia Reinforced Glass-ionomers with and without Microhydroxyapatite
Statement of problem: Hardness of restorative materials like glass-ionomer is an important factor in the longevity of restoration. Objectives: The aim of this study was to evaluate the microhardness of glass-ionomer modi...
The Effect of Time Intervals on Heat Transfer to the Implant-Bone Interface during Preparation of a Titanium Abutment: An in Vitro Study
Statement of Problem: Thermal injury during dental implant placement and restoration is a clinical concern as it may cause bone damage and compromise osseointegration. The threshold level for heat-induced cortical bone n...