Jute fibre reinforced plastic: evaluation of application based properties
Journal Title: Carbon - Science and Technology - Year 2015, Vol 7, Issue 1
Abstract
A fibre extracted from jute is a budding component identified for its potential application in composites. It is imperative to evaluate the parametric and property based features to determine its suitability. In this research study, considering the possible application of the fibre composites, the aptness of these fibres are examined with respect to their physical, mechanical [by layered manufacturing technique(LM)] and thermal properties. This study focuses on evaluating the properties and behaviour of raw Jute fibres and NaOH surface treated fibres. Subsequently, the fibres are subjected to thermo-gravimetry tests. The outcome of the thermal analysis clearly indicates that the temperature peak shifts to a higher region in the treated fibre compared to raw fibre. The overall observation strongly emphasize that the physical properties and the thermal behaviour of jute fibre are enhanced after surface treatments which makes it more feasible for its application in composite structures.
Authors and Affiliations
J. B. Sajin, R. Sivasubramanian, R. Nagalingam, M. Sivakumar
Dry fermentation technology for utilization of Bio-energy crops/crop residues for biogas production
Indian state Punjab produces 160 lakh tones of paddy every year. More than this quantity of paddy, straw is also produced which is not properly utilized. Paddy is burnt in the farmer’s fields itself, which produces lot o...
Effect of temperature on the crystallite size of Lanthanum Cerium Oxide (La2Ce2O7) and its optical properties
The effect of the calcination process on the crystallite size and optical properties of Lanthanum Cerium Oxide (La2Ce2O7) nanopowders synthesized using co-precipitation process were reported. X-ray diffraction analysis r...
Oxygen reduction activity of carbon fibers cathode, and application for current generation from the NAD+ and NADH recycling reaction
Carbon fibers treated at 700 oC for 10 min. were found to have O2 reduction activity when being used as a cathode. The special type of partition combined with both cationic and anionic exchange membranes was applied betw...
Effect of multipass cutting on surface roughness in wire electrical discharge machining of metal matrix composites
The workpiece produced by wire electrical discharge machining (WEDM) has the surface variations caused by simultaneous heating and cooling process during machining. The thermally affected layers have great effect on mech...
The effect of PTSA on preparation of mesophase carbon spheres
Mesophase spheres have been synthesized by heat-treating a medium coal tar pitch at 420 ºC for 2 hours in the presence of P-toluene sulphonic acid (PTSA). The effect of PTSA on synthesis of mesophase spheres had been stu...