A cohesive zone model to simulate the hydrogen embrittlement effect on a high-strength steel
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
The present work aims to model the fracture mechanical behavior of a high-strength low carbon steel, AISI 4130 operating in hydrogen contaminated environment. The study deals with the development of 2D finite element cohesive zone model (CZM) reproducing a toughness test. Along the symmetry plane over the crack path of a C(T) specimen a zero thickness layer of cohesive elements are implemented in order to simulate the crack propagation. The main feature of this kind of model is the definition of a traction-separation law (TSL) that reproduces the constitutive response of the material inside to the cohesive elements. Starting from a TSL calibrated on hydrogen non-contaminated material, the embrittlement effect is simulated by reducing the cohesive energy according to the total hydrogen content including the lattice sites (NILS) and the trapped amount. In this perspective, the proposed model consists of three steps of simulations. First step evaluates the hydrostatic pressure. It drives the initial hydrogen concentration assigned in the second step, a mass diffusion analysis, defining in this way the contribution of hydrogen moving across the interstitial lattice sites. The final stress analysis, allows getting the total hydrogen content, including the trapped amount, and evaluating the new crack initiation and propagation due to the hydrogen presence. The model is implemented in both plane strain and plane stress configurations; results are compared in the discussion. From the analyses, it resulted that hydrogen is located only into lattice sites and not in traps, and that the considered steel experiences a high hydrogen susceptibility. By the proposed procedure, the developed numerical model seems a reliable and quick tool able to estimate the mechanical behavior of steels in presence of hydrogen.
Authors and Affiliations
G. Gobbi, C. Colombo, L. Vergani
Keywords
Related Articles
- EP ID EP106761
- DOI 10.3221/IGF-ESIS.35.30
- Views 65
- Downloads 0
Temporal peculiarities of brittle fracture of rocks and concrete
When we want to compare the strength of two materials, we compare the table values of quasi-static strength. However results of some experiments show that the strength ratio of the materials can change with increas...
Propagazione di fratture longitudinali in gasdotti caratterizzati da bassa duttilità
Il presente lavoro propone l’analisi di propagazione di una frattura fragile longitudinale di un gasdotto interrato basata sulla valutazione dell’energy release rate. Viene illustrata l’implementazione della sudd...
Fractography as a tool to assess the occurrence of fatigue fractures in complex microstructure structural components
Fractographic assessment of fatigue fractures may be difficult if they occur in metallic components characterized by low ductility complex microstructures. In these cases reconciliation of known fatigue ruptu...
Crack path in liquid metal embrittlement:experiments with steels and modeling
We review the recent experimental clarification of the fracture path in Liquid Metal Embrittlement with austenitic and martensitic steels. Using state of the art characterization tools (Focused Ion Beam and T...
A critical review of fracture mechanics as a tool for multiaxial fatigue life prediction of plastics1
Plastics belong to the most complex and probably least understood engineering materials of today. Combining the best aspects of design, mechanical properties and manufacturing, the structural integrity of plastic...