A plastic stress intensity factor approach to turbine disk structural integrity assessment

Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 37

Abstract

 This study based on a new fracture mechanics parameter is concerned with assessing the integrity of cracked steam turbine disk which operate under startup-shutdown cyclic loading conditions. Damage accumulation and growth in service have occurred on the inner surface of slot fillet of key. In order to determine elastic-plastic fracture mechanics parameters full-size stress-strain state analysis of turbine disk was performed for a quote-elliptical part-through cracks under considering loading conditions. As a result distributions of elastic and plastic stress intensity factors along crack front in slot fillet of key of turbine disk depending on surface crack form are defined. An engineering approach to the prediction of carrying capacity of cracked turbine disk which is sensitive to the loading history at maintenance is proposed. The predictions of the rate of crack growth and residual lifetime of steam turbine disk are compared for elastic and elastic-plastic solutions. It is shown that the previously proposed elastic crack growth models provide overestimate the lifetime with respect to the present one. An advantage to use the plastic stress intensity factor to characterize the fracture resistance as the self-dependent unified parameter for a variety of turbine disk configurations rather than the magnitude of the elastic stress intensity factors alone is discussed

Authors and Affiliations

V. Shlyannikov, A. Zakharov, R. Yarullin

Keywords

Related Articles

 Influence of different sizes of concrete and roller compacted concrete on double-K fracture parameters

 Affected by physical properties of various components, characteristics and stress states of junction surface and other multiple factors, concrete, as a kind of multi-phase composite material, has complicated ...

 Can Keff be assumed as the driving force for fatigue crack growth?

 This work raises some new questions about the validity of blindly assuming that Elber’s effective stress intensity factor is the actual fatigue crack driving force, and that as so it can be used to explain all loa...

 The effect of varying loading directions and loading levels on crack growth at 2D- and 3D-mixed-mode-loadings

  While product’s operation the loading situation commonly changes. The local loading situation on an existing crack then can shift to a combined loading, composed of mode I, mode II and mode III, and consequently i...

 Experimental estimation of the heat energy dissipated in a volume surrounding the tip of a fatigue crack

 Fatigue crack initiation and propagation involve plastic strains that require some work to be done on the material. Most of this irreversible energy is dissipated as heat and consequently the material temperature&...

 Recent developments in multi-parametric three-dimensional stress field representation in plates weakened by cracks and notches

 The paper deals with the three-dimensional nature and the multi-parametric representation of the stress field ahead of cracks and notches of different shape. Finite thickness plates are considered, under different...

Download PDF file
  • EP ID EP107079
  • DOI 10.3221/IGF-ESIS.37.25
  • Views 57
  • Downloads 0

How To Cite

V. Shlyannikov, A. Zakharov, R. Yarullin (2016).  A plastic stress intensity factor approach to turbine disk structural integrity assessment. Frattura ed Integrità Strutturale, 10(37), 193-199. https://europub.co.uk./articles/-A-107079