Characterisation of crack tip fields under non-uniform fatigue loading
Journal Title: Frattura ed Integrità Strutturale - Year 2013, Vol 7, Issue 25
Abstract
The paper analyses previously reported work, which uses digital image correlation to measure fatigue crack closure. As well as determining crack opening loads, the information on crack shape may be used to estimate the stress intensity factor, as well as other parameters in more complex models of crack tip fields. A number of specimens were subjected to single overload cycles, which produced a significant retardation in crack growth rate. The method previously applied to the analysis of constant amplitude loading is here used to analyse the single overload case. The stress intensity factor history is found to be very different in the two cases and the consequences of this observation for analysis of fatigue crack propagation are discussed.
Authors and Affiliations
D. Nowell, M. E. Kartal, P. E. P. de Matos
Keywords
Related Articles
- EP ID EP156660
- DOI 10.3221/IGF-ESIS.25.01
- Views 54
- Downloads 0
An efficient Bouc & Wen approach for seismic analysisof masonry tower
The assessment of existing masonry towers under exceptional loads, such as earthquake loads,requires reliable, expedite and efficient methods of analysis. These approaches should take into account boththe randomnes...
Comparative study of multiaxial fatigue methods applied to welded joints in marine structures
Marine structures are particularly prone to action of waves, winds and currents with stochastically varying composition, intensities and directions. Therefore, resultant stresses may cause multiaxial fatigue in&nb...
Fatigue life estimation in welded joints under multiaxial loadings
Welded joints are frequently locations for cracks initiation and propagation that may cause fatigue failure of engineering structures. Biaxial or triaxial stress-strain states are present in the vicinity of welded joint...
Effect of defect length on rolling contact fatigue crack propagation in high strength steel
The objective of the present paper is to clarify the effect of defect length in depth direction on rolling contact fatigue (RCF) crack propagation in high strength steel. RCF test and synchrotron radiation micro&n...
Computed Tomography analysis of damage in composites subjected to impact loading
The composites, used in the transportation engineering, include different classes with a wide range of materials and properties within each type. The following different typologies of composites have been investigated:...