Controlling fatigue crack paths for crack surface marking and growth investigations
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
While it is well known that fatigue crack growth in metals that display confined slip, such as high strength aluminium alloys, develop crack paths that are responsive to the loading direction and the local microstructural orientation, it is less well known that such paths are also responsive to the loading history. In these materials, certain loading sequences can produce highly directional slip bands ahead of the crack tip and by adjusting the sequence of loads, distinct fracture surface features or progression marks, even at very small crack depths can result. Investigating the path a crack selects in fatigue testing when particular combinations of constant and variable amplitude load sequences are applied is providing insight into crack growth. Further, it is possible to design load sequences that allow very small amounts of crack growth to be measured, at very small crack sizes, well below the conventional crack growth threshold in the aluminium alloy discussed here. This paper reports on observations of the crack path phenomenon and a novel test loading method for measuring crack growth rates for very small crack depths in aluminium alloy 7050-T7451 (an important aircraft primary structural material). The aim of this work was to firstly generate short- crack constant amplitude growth data and secondly, through the careful manipulation of the applied loading, to achieve a greater understanding of the mechanisms of fatigue crack growth in the material being investigated. A particular focus of this work is the identification of the possible sources of crack growth retardation and closure in these small cracks. Interpreting these results suggests a possible mechanism for why small fatigue crack growth through this material under variable amplitude loading is faster than predicted from models based on constant amplitude data alone.
Authors and Affiliations
S. Barter, P. White, M. Burchill
Keywords
Related Articles
- EP ID EP95867
- DOI 10.3221/IGF-ESIS.35.16
- Views 78
- Downloads 0
A consistency assessment of coupled cohesive zonemodels for mixed-mode debonding problems
Due to their simplicity, cohesive zone models (CZMs) are very attractive to describe mixed-modefailure and debonding processes of materials and interfaces. Although a large number of coupled CZMs havebeen proposed,...
Relation between the plastic instability and fracture of tensile tested Cu-Sn alloys investigated with the application of acoustic emission technique
The work concerns the application of the acoustic emission (AE) method in testing the mechanical properties of continuously cast industrial tin bronze CuSn6P, which reveals tendencies to instable plastic flow ...
Effects of microstructure and crystallography on crack path and intrinsic resistance to shear-mode fatigue crack growth
The paper focuses on the effective resistance and the near-threshold growth mechanisms in the ferritic-pearlitic and the pure pearlitic steel. The influence of microstructure on the shear-mode fatigue crack g...
Shortcuts in multiple dimensions: the multiaxial racetrack filter
Filtering techniques have been proposed for multiaxial load histories, usually aiming to filter out non-reversals, i.e. sampling points that do not constitute a reversal in any of its stress or strain components....
Computed Tomography analysis of damage in composites subjected to impact loading
The composites, used in the transportation engineering, include different classes with a wide range of materials and properties within each type. The following different typologies of composites have been investigated:...