Effects of large amounts of hydrogen on the fatigue crack growth behavior of torsional prestrained carbon steel
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 35
Abstract
The effects of large amounts of hydrogen on the fatigue crack growth properties of torsional prestrained ferritic–pearlitic low-carbon steel were investigated. Hydrogen-precharged specimens were produced by conducting cathodic charge to the virgin material and to torsional prestrained JIS-S10C and JISS25C steels (hereafter S10C and S25C steels). Rotating bending fatigue tests were conducted in air at room temperature. Hydrogen content, CH, increased with torsional prestrain for both S10C and S25C steels; the CH of the torsional prestrained S25C steel precharged with hydrogen was lower than that of S10C at the same torsional prestrain. No clear difference between the maximum CH values of the torsional fractured S10C and S25C hydrogen-precharged steel specimens. With respect to crack initiation, there was no obvious difference between the uncharged and precharged specimens in spite of the large amount of CH induced by torsional prestrain. The acceleration of fatigue crack growth by hydrogen was the main cause of the decreased fatigue life. For the virgin material, hydrogen had no obvious effect on the fatigue crack growth rate. In contrast, for the torsional prestrained materials, the acceleration ratios, {(da/dN)H/(da/dN)U}, increased with the torsional prestrain and CH. However, {(da/dN)H/(da/dN)U} did not exceed the value of about 30, even when a large amount of hydrogen was charged (10.0 ≤ CH ≤ 30.3 mass ppm). A hydrogen content threshold was found; hydrogen content above this limit enhances the growth of the non-propagated crack, even for metals with lower hardness (HV < 200).
Authors and Affiliations
Yuta Matsuda, Hiroshi Nishiguchi, Takayuki Fukuda
Keywords
Related Articles
- EP ID EP106731
- DOI 10.3221/IGF-ESIS.35.01
- Views 66
- Downloads 0
An all-in-one numerical methodology for fretting wear and fatigue life assessment
Many mechanical components such as, bearing housings, flexible couplings and spines or orthopedic devices are simultaneously subjected to a fretting wear and fatigue damage. For this reason, the combined stud...
Recast layers on high speed steel surface after electrical discharge treatment in electrolyte
In this work are discussed some experimental data about the obtaining of recast layers on the surface of high speed tool steel after electrical discharge treatment in electrolyte. The electrical discharge treatme...
Biaxial fatigue behavior of a powder metallurgical TRIP steel
Multiaxial fatigue behavior is an important topic in critical structural components. In the present study the biaxial-planar fatigue behavior of a powder metallurgical TRIP steel (Transformation Induced Plasticity...
Influence of temperature and exploitation period on fatigue crack growth parameters in different regions of welded joints
The influence of exploitation period and temperature on the fatigue crack growth parameters in different regions of a welded joint is analysed for new and exploited low-alloyed Cr-Mo steel A-387 Gr. B. The pa...
Estimation of fretting fatigue life using a multiaxial stress-based critical distance methodology
This work presents a methodology for life estimation of mechanical couplings subjected to fretting fatigue. In this approach, a stress-based multiaxial fatigue parameter is evaluated at a critical distance below t...