Experimental investigation of effect of specimen thickness on fracture toughness of Al-TiC composites
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 37
Abstract
In this paper, the macro and micro-mechanical fracture behavior was studied for aluminum (Al6061) alloy matrix, reinforced with various proportions of TiC particles such as 3wt%, 5wt% and 7wt%. The Al6061-TiC metal matrix composites were produced by stir casting method to ensure uniform distribution of the TiC particulates in the Al matrix. The compact tension (CT) specimens were machined according to ASTM E399 specifications to evaluate the fracture toughness for Al6061-TiC metal matrix composites. The CT specimens were machined for crack to width (a/W) ratio of 0.5 and thickness to width (B/W) ratios of 0.2 to 0.7 with an increment of 0.1. Load versus crack mouth opening displacement (CMOD) data was plotted to estimate stress intensity factor KQ for various thicknesses of the specimen. The fracture toughness KIC was obtained by plotting stress intensity factor versus thickness to width ratios of specimen data. The fracture toughness of these composites varied between 16.4-19.2 MPa√m. Scanning Electron Microscope (SEM) studies was made on the fractured surface of the specimens to understand the micro-mechanisms of failure involved in these composites. Void initiation is more significant in the matrix near the interface. The micro-cracks grow from these micro-voids and crack propagates by linking these micro cracks locating the crack path preferentially in the matrix adjacent to the interface indicating ductile fracture.
Authors and Affiliations
M. Raviraj, C. Sharanaprabhu, G. Mohankumar
Keywords
Related Articles
- EP ID EP154289
- DOI 10.3221/IGF-ESIS.37.47
- Views 65
- Downloads 0
Plastic flow equations for the local strain approach in the multiaxial case
This paper presents a system of plastic flow equations which uses and generalizes to the multiaxial case a number of concepts commonly employed in the so-called Local Strain Approach to low cycle fatigue. Eve...
On the influence of T-Stress on photoelastic analysis under pure mode II loading
According to the classical definition for in-plane modes of crack deformation, the constant stress term T exists only in the presence of mode I. However, recent studies show that this term can exist in mode II cond...
Modification of creep and low cycle fatigue behaviour induced by welding
In this work, the mechanical properties of Waspaloy superalloy have been evaluated in case of welded repaired material and compared to base material. Test program considered flat specimens on base and TIG welded...
Acoustic emission characteristics of instability process of a rock plate under concentrated loading
It can facilitate the understanding of the mechanical properties and failure laws of rocks to research on the rock failure mechanism and evolution characteristics of Acoustic Emission (AE). Under the concentrated...
Study of the conditions of fracture at explosive compaction of powders
Joint theoretical and experimental investigations have allowed to realize an approach with use of mathematical and physical modeling of processes of a shock wave loading of powder materials.In order to gain a bette...