Fatigue crack growth of aluminium alloy 7075-T651 under non-proportional mixed mode I and II loads
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 38
Abstract
This study aims to investigate fatigue growth behaviour in AA7075-T651 under non-proportional mixed mode I and II loads. Fatigue tests were performed under cyclic tension and torsion using a thin-walled tubular specimen with a key-hole style crack starter. After the generation of a single-side mode I pre-crack, varied forms of mixed mode loads were applied, which in most cases led to a short distance coplanar growth followed by a long and stable crack path deviation. It was found that under most of the non-proportional mixed mode load cases, the direction of the deviated crack path could not be reasonably predicted using the commonly accepted maximum tangential stress criterion. Meanwhile, in some cases, the crack path directions could be approximately predicted using the maximum shear stress criterion. It was also confirmed for the first time that a long, stable and noncoplanar shear mode fatigue crack growth could be produced in AA7075T651 under non-proportional mixed mode I and II loads. ©2016 Commonwealth of Australia
Authors and Affiliations
Xiaobo Yu, Ling Li, Gwénaëlle Proust
Keywords
Related Articles
- EP ID EP118206
- DOI 10.3221/IGF-ESIS.38.20
- Views 72
- Downloads 0
Case studies in numerical simulation of crack trajectories in brittle materials
Statistical Fracture Mechanics, formalism of few natural ideas is applied to simulation of crack trajectories in brittle material. The “diffusion approximation” of the crack diffusion model represents crack traject...
Inter-laminar shear stress in hybrid CFRP/austenitic steel
Bolted joints are the most common solution for joining composite components in aerospace structures. Critical structures such as wing to fuselage joints, or flight control surface fittings use bolted joining tech...
Limit analysis on FRP-strengthened RC members
Reinforced concrete (RC) members strengthened with externally bonded fiber-reinforced-polymer(FRP) plates are numerically investigated by a plasticity-based limit analysis approach. The key-concept of thepresent ap...
Multi-parameter approximation of stress field in a cracked specimen using purpose-built Java applications
A quality of multi-parameter approximation of the stress and displacement fields around a crack tip in a non-brittle material test specimen is studied in the paper. The stress field approximation using Williams p...
Implementation of a damage model in a finite element program for computation of structures under dynamic loading
This work is a numerical simulation of nonlinear problems of the damage process and fracture of quasi-brittle materials especially concrete. In this study, we model the macroscopic behavior of concrete material,...