Fatigue life assessment of a non-load carrying fillet joint considering the effects of a cyclic plasticity and weld bead shape
Journal Title: Frattura ed Integrità Strutturale - Year 2016, Vol 10, Issue 38
Abstract
Fatigue life depends strongly on irreversible contributions that accumulate during cyclic loading and unloading of structures. However, the correct identification of the loading path in terms of uniaxial or multi-axial stress states, proportional or non-proportional loading is essential because these factors can significantly alter the material response. In this study, finite element analysis was conducted to assess the fatigue crack initiation life of a non-load carrying fillet joint by considering weld bead shape and a cyclic plasticity accumulation during fatigue loading, which is a main cause of crack initiation. Cyclic plasticity behaviour including cyclic hardening and softening together was investigated with an unconventional plasticity model called the subloading surface model and extended to include both elastic boundary and cyclic damage concepts. The cyclic plasticity model can capture realistic plastic strain accumulation during high cycle fatigue under macroscopically elastic stressing conditions
Authors and Affiliations
S. Tsutsumi, K. Morita, R. Fincato, H. Momii
Keywords
Related Articles
- EP ID EP107300
- DOI 10.3221/IGF-ESIS.38.33
- Views 92
- Downloads 0
A study of the stored energy in titanium under deformation and failure using infrared data
The work is devoted to the experimental study of heat dissipation caused by plastic deformation and failure processes taking place in a titanium alloy Ti-4.2Al-1.6Mn. To investigate the spatial and time evolution o...
Multi-parameter crack tip stress state description for estimation of fracture process zone extent in silicate composite WST specimens
For wedge splitting test specimens, the stress and displacement fields both in the vicinity and also in larger distance from the crack tip are investigated by means of numerical methods. Several variants of boundar...
Influence of boundary conditions on the response ofmultilayered plates with cohesive interfaces anddelaminations using a homogenized approach
Stress and displacement fields in multilayered composites with interfacial imperfections, such asimperfect bonding of the layers or delaminations, or where the plies are separated by thin interlayers allowingrelati...
New experimental techniques for fracture testing of highly deformable materials
A new experimental method for measuring strain fields in highly deformable materials has been developed. This technique is based on an in-house developed Digital Image Correlation (DIC) system capable of accu...
Design of a novel magnetorheological damper with internal pressure control
In this work we designed and manufactured a novel magnetorheological (MR) fluid damper with internal pressure control. Previous authors’ works showed that the yield stress τB of MR fluids depends both on the magne...