In situ observation of rolling contact fatigue cracks by laminography using ultrabright synchrotron radiation
Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 34
Abstract
In rolling contact fatigue (RCF), cracks usually initiate from inclusions beneath the surface and propagate to the contact surface. In the present study, synchrotron radiation computed laminography (SRCL) imaging was performed to observe flaking defects during the RCF of a high-strength steel. Specially fabricated inclusion-rich steel plate specimens were employed in the experiments. For the in situ observation of crack propagation, a compact RCF testing machine was developed, and a 4D analysis scheme was applied to the data obtained by SRCL. RCF tests were carried out near the measurement hatch of the beam line used SRCL to enable the successive observation of crack initiation and growth behaviors. Specimens before and after the occurrence of flaking were observed by SRCL, and flaking defects and cracks under the surface were successfully detected. As a result, details of the crack initiation and flaking process in RCF could be discussed. Shear-type horizontal cracks were found to initiate after the initiation and propagation of tensile-type vertical cracks along inclusions, where the face of the vertical cracks was perpendicular to the rolling direction and rolling surface. Therefore, the formation of vertical cracks is considered to affect shear-type crack formation and flaking, where the shape and length of inclusions also affect the initiation and propagation of vertical cracks.
Authors and Affiliations
Y. Nakai, D. Shiozawa, S. Kikuchi, K. Sato, T. Obama
Keywords
Related Articles
- EP ID EP133172
- DOI 10.3221/IGF-ESIS.34.26
- Views 54
- Downloads 0
Recent developments in multi-parametric three-dimensional stress field representation in plates weakened by cracks and notches
The paper deals with the three-dimensional nature and the multi-parametric representation of the stress field ahead of cracks and notches of different shape. Finite thickness plates are considered, under different...
Studio delle prestazioni di giunzioni incollate ibride
Le giunzioni ibride sono giunzioni in cui coesistono due differenti tipologie di giunzione, di cui una è l’incollaggio. L’articolo mostra i risultati di una campagna sperimentale volta a caratterizzare le prestazioni di...
A mechanical model for FRP-strengthened beams in bending
We analyse the problem of a simply supported beam, strengthened with a fibre-reinforced polymer (FRP) strip bonded to its intrados and subjected to bending couples applied to its end sections. A mechanical model is...
On the preparation and characterization of thin NiTi shape memory alloy wires for MEMS
Shape memory alloy (SMA) wires are employed as actuators in small devices for consumer electronics, valves and automotive applications. Because of the continued miniaturization of all the industrial products, nowad...
Mechanical characterization of basalt woven fabric composites: numerical and experimental investigation
Basalt fabric composite, with different twill wave reinforcements, i.e. twill 2/2 and twill 1/3, have been studied in this work by means of experimental tests and numerical finite element (FE) simulations. As fabri...