Kinetics of fatigue crack growth and crack paths in the old puddled steel after 100-years operating time
Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 34
Abstract
The goal of the authors’ investigations was determination of the fatigue crack growth in fragments of steel structures (of the puddled steel) and its cyclic behavior. Tested steel elements coming from the turn of the 19th and 20th were gained from still operating ancient steel construction (a main hall of Railway Station, bridges etc.). This work is a part of investigations devoted to the phenomenon of microstructural degradation and its potential influence on their strength properties. The analysis of the obtained results indicated that those long operating steels subject to microstructure degradation processes consisting mainly in precipitation of carbides and nitrides inside ferrite grains, precipitation of carbides at ferrite grain boundaries and degeneration of pearlite areas [1, 2]. It is worth noticing that resistance of the puddled steel to fatigue crack propagation in the normalized state was higher. The authors proposed the new kinetic equation of fatigue crack growth rate in such a steel. Thus the relationship between the kinetics of degradation processes and the fatigue crack growth rate also have been shown. It is also confirmed by the materials research of the viaduct from 1885, which has not shown any significant changes in microstructure. The non-classical kinetic fatigue fracture diagrams (KFFD) based on deformation () or energy (W) approach was also considered. In conjunction with the results of low- and high-cycle fatigue and gradual loss of ductility as a consequence (due to the microstructural degradation processes) - it seems to be a promising construction of the new kinetics fatigue fracture diagrams with the energy approach.
Authors and Affiliations
G. Lesiuk, M. Szata
Keywords
Related Articles
- EP ID EP117573
- DOI 10.3221/IGF-ESIS.34.31
- Views 53
- Downloads 0
Tests in tension-torsion conditions with descending sections of strain curve construction
The paper is devoted to theoretical and experimental investigation of materials behavior on postcritical deformation stage (strain softening). Tests results, which confirm theoretical justification of specimen conf...
Atomistic modeling of different loading paths in single crystal copper and aluminum
Utilizing molecular dynamics (MD) integration model we have investigated some of the relevant physical processes caused by different loading paths at the atomic level in Cu and Al monocrystal specimen. Interaction...
Crack growth simulation in heterogeneous material by S-FEM and comparison with experiments
Fully automatic fatigue crack growth simulation system is developed using S-version FEM (SFEM). This system is extended to fracture in heterogeneous material. In the heterogeneous material, crack tip stress field...
On the crack path under mixed mode loading on PUR foams
In this paper are presented the crack initiation angles obtained in polyurethane (PUR) foams under mixed mode loading. Closed cell rigid PUR foams having three different densities 100, 145, and 300 kg/m3 were inve...
Crack growth threshold under hold time conditions in DA Inconel 718 – A transition in the crack growth mechanism
Aeroengine manufacturers have to demonstrate that critical components such as turbine disks, made of DA Inconel 718, meet the certification requirements in term of fatigue crack growth. In order to be more re...