Random accumulated damage evaluation under multiaxial fatigue loading conditions
Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 33
Abstract
Multiaxial fatigue is a very important physical phenomenon to take into account in several mechanical components; its study is of utmost importance to avoid unexpected failure of equipment, vehicles or structures. Among several fatigue characterization tools, a correct definition of a damage parameter and a load cycle counting method under multiaxial loading conditions show to be crucial to estimate multiaxial fatigue life. In this paper, the SSF equivalent stress and the virtual cycle counting method are presented and discussed, regarding their physical foundations and their capability to characterize multiaxial fatigue damage under complex loading blocks. Moreover, it is presented their applicability to evaluate random fatigue damage.
Authors and Affiliations
V. Anes, L. Reis, M. de Freitas
Keywords
Related Articles
- EP ID EP116919
- DOI 10.3221/IGF-ESIS.33.35
- Views 54
- Downloads 0
Investigation of mixed mode-I/II fracture problems - Part 2: evaluation and development of mixed mode-I/II fracture criteria
In this study, experimental and numerical results of compact tension shear (CTS) specimen and a new specimen type under in-plane mixed mode (Mode-I/II) loading conditions are compared with existing inplane mi...
A new formulation for estimating maximum stress intensity factor atthe mid plane of a SENB specimen: Study based on 3D FEA
In this investigation, three-dimensional elastic finite element analyses have been conducted tocompute the stress intensity factor (KI) in a SENB specimen with varied thickness (B) and crack-length to widthratio (a...
On the applicability of multi-surface, two-surface and non-linear kinematic hardening models in multiaxial fatigue
In this work, a comparison between NLK and Mróz-Garud’s multi-surface formulations is presented. A unified common notation is introduced to describe the involved equations, showing that the Mróz-Garud model can b...
Pressure vessels design methods using the codes, fracture mechanics and multiaxial fatigue
This paper gives a highlight about pressure vessel (PV) methods of design to initiate new engineers and new researchers to understand the basics and to have a summary about the knowhow of PV design. This understan...
Numerical investigation on stress corrosion cracking behavior ofdissimilar weld joints in pressurized water reactor plants
There have been incidents recently where stress corrosion cracking (SCC) observed in the dissimilarmetal weld (DMW) joints connecting the reactor pressure vessel (RPV) nozzle with the hot leg pipe. Due to thecomple...