PHASE EQUILIBRIA IN THE Al2O3–TiO2–Y(Er)2O3 SYSTEMS AT 1400 ºС
Journal Title: Вісник Одеського національного університету. Хімія - Year 2017, Vol 22, Issue 4
Abstract
The aim of this investigation is the construction of isothermal sections for the Al2O3-TiO2-Y(Gd)2O3 phase diagrams at 1400ºС as part of systematic investigations of Al2O3-TiO2-Ln2O3 (Ln=lanthanides, Y) systems. The 1400°C was taken as the temperature, at which no liquid phases are expected in the both systems. The isothermal sections at 1400 °С for the Al2O3– TiO2–Y(Er)2O3 phase diagrams were constructed for the first time. Samples were prepared by a chemical method. Samples were annealed in air at 1400°С for 80 hours and cooled in the furnace. This temperature value was selected with a view to provide possibility of phase transformations character studies. New phases and appreciable solubility regions based on the components and binary compounds were not found, as predicted. Triangulation of the systems is determined by the phase Y(Er)2T2O7, which is in equilibria with compounds Al2TiO5, Y(Er)3Al5O12, Y(Er)AlO3, Y(Er)4Al2O9 and components TiO2 and Al2O3. The structures of isothermal sections of the both systems are similar. The systems are triangulated into six secondary triangles, in which three-phase eutectic are expected. In five quasibinary sections two-phase eutectic should expect to exist. The obtained results will make a significant contribution to the understanding of interactions between the components in the systems studied.This systems offer a number of promising opportunities such as high-temperature structural composites based on directionally solidified two-phase and three-phase eutectic materials, solid electrolytes (SOFCs, oxygen sensors, film for electronic devices, etc.), promising to accumulate water, immobilizing materials for nuclear industry, tough ceramics, catalysts carriers, wear- and corrosion-resistant ceramic coatings and super refractories.
Authors and Affiliations
I. S. Tyshchenko, M. S. Glabay, A. A. Makudera, S. M. Lakiza, E. V. Dudnik
Keywords
Related Articles
- EP ID EP336078
- DOI 10.18524/2304-0947.2017.4(64).115934
- Views 82
- Downloads 0
THERMAL STABILITY OF 1,8-NAPHTHALIMIDE TETRAALKYLAMMONIUM SALTS
The synthesis of tetraalkylammonium 1,8-naphthalimides was performed in benzene-5% NaOH aqueous solution at room temperature by anion exchange and subsequent extraction of the desired salts into the organic phase with yi...
3d-METAL COMPLEXES WITH BARBITURIC ACID DERIVATIVES
The various aspects of the 3d-metal complexes with barbiturates and uric acid chemistry such as composition, structure, physicochemical properties, possible fields of application – have been illustrated in this review
PHASE EQUILIBRIA IN THE ZrO2–Yb2O3 SYSTEM AT 1100 °С
Phase equilibria in the binary ZrO2 – Yb2O3 system at 1100°C were studied by X-ray diffraction and petrography in the overall concentration range. The samples of different compositions have been prepared from nitrate aci...
ADSORPTION AND PHYSICOCHEMICAL PROPERTIES OF NATURAL MONTMORILLONITES AND THEIR MODIFIED FORMS
The data, earlier published and obtained by us, concerning an influence of various factors on physicochemical properties and structural parameters for montmorillonites of different origin are summarized. Some regularitie...
MECHANISMS OF THE COMPLEX FORMATION BY d-METALS ON POROUS SUPPORTS AND THE CATALYTIC ACTIVITY OF THE FORMED COMPLEXES IN REDOX REACTIONS
The catalytic activity of supported complexes of d metals in redox reactions with participation of gaseous toxicants, PH3, CO, O3, and SO2, depends on their composition. Owing to the variety of physicochemical and struct...