Prediction of maximum casting defect size in MAR-M-247 alloy processed by hot isostatic pressing
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2015, Vol 22, Issue 1
Abstract
Nickel based MAR-M-247 superalloy treated by hot isostatic pressing was investigated with the aim to identify the influence of casting defect size on fatigue life. Two testing temperatures of 650 and 800°C and one stress amplitude were chosen for fatigue tests. The Murakami approach and the largest extreme value distribution theory were applied. It has been found that the maximum size of casting defects in a specimen can be satisfactorily predicted. Fatigue life of specimens was in the good agreement with assumptions based on the evaluation and prediction of the casting defect size.
Authors and Affiliations
Miroslav Smid, Stanislava Fintova, Ludvik Kunz, Pavel Hutar, Karel Hrbacek
Keywords
Related Articles
- EP ID EP122100
- DOI -
- Views 98
- Downloads 0
MICROSTRUCTURE AND MECHANICAL PROPERTIES DEGRADATION OF CrMo CREEP RESISTANT STEEL OPERATING UNDER CREEP CONDITIONS
In this contribution microstructure degradation of a steam tube is analysed. The tube is made of CrMo creep resistant steel and was in service under creep conditions at temperature 530°C and calculated stress level in th...
THE ANALYSIS OF CAUSES OF LORRY PISTON COMBUSTION ENGINE DAMAGE
The article deals with analysis of causes of lorry piston combustion engine damage. For docummentation and analysis of causes was used macroscopical, microscopical and scanning electron microscopy. The analysis showed th...
CORRELATION BETWEEN HARDNESS AND TENSILE PROPERTIES IN ULTRA-HIGH STRENGTH DUAL PHASE STEELS – SHORT COMMUNICATION
The possibility to predict yield strength, strength limit, fatigue live estimation as well as other mechanical properties depending on values of materials hardness is commonly known and it is often used in practice. The...
THE QUALITY OF MATERIALS APPLIED FOR SLEWING BEARING RACEWAY – TECHNICAL PAPER
Selected slewing bearings and their application have been described in this article. Basic causes of the damage pitch surfaces of slewing bearings have been analyzed and examples of the damage have been presented as well...
EFFECTIVNESS OF THE FATIGUE CRITERIA FOR COMBINED BENDING – TORSION LOADING
Most of mechanical components in the engineering are frequently subjected to combined loading, which can lead to sudden fatigue failure. In present work the fatigue life of plasma-nitrided and virgin specimens is studied...