Rheological, thermal and tensile properties of PE/nanoclay nanocomposites and PE/nanoclay nanocomposite cast films
Journal Title: Polyolefins Journal - Year 2018, Vol 5, Issue 1
Abstract
The effects of three different mixers, two different feeding orders and nanoclay content on the structure development and rheological properties of PE/nanoclay nanocomposite samples were investigated. Fractional Zener and Carreau–Yasuda models were applied to discuss the melt linear viscoelastic properties of the samples. Moreover, scaling law for fractal networks was used to quantify clay dispersion depended on the PE matrix structure. The simultaneous feeding resulted in better dispersion and melt intercalation for the nanoclay as compared to the compatibilizer/nanoclay masterbatch feeding. The twin screw extruder (Brabender DSE 25 model) showed greater potential for melt intercalation of PE/nanoclay as compared to the internal mixers (Brabender W50 and Haake Rheomix 3000 batch mixer) . Comparing the thermal Analysis of PE, PE/PE-g-MA and PE/nanoclay samples by DSC technique showed the opposite effect of the compatibilizer and the nanoclay to crystallization behavior of PE. PE/nanoclay cast film samples were produced with three different draw ratios. X-ray diffraction structural analysis in conjunction with the melt linear viscoelastic measurements confirmed that the PE/nanoclay cast film produced at higher draw ratio showed the more effective melt intercalation. Tensile test showed the machine direction modulus and yield strength of both PE and PE/nanoclay cast film samples reduced with increase of draw ratio
Authors and Affiliations
Mehdi Hajiabdolrasouli, Amir Babaei
Keywords
Related Articles
- EP ID EP283210
- DOI 10.22063/POJ.2017.1500
- Views 115
- Downloads 0
Introduction of titanium species into fluorine-modified SiO2- supported Cr-V bimetallic catalyst for ethylene polymerization and ethylene/1-hexene copolymerization
Chromium-vanadium (Cr-V) bimetallic catalysts are prepared by the introduction of vanadium into the Phillips catalyst which is one of the most significant industrial ethylene polymerization catalysts for tuning the Phill...
Storage time effect on dynamic structure of MgCl2.nEtOH adducts in heterogeneous Ziegler-Natta catalysts
Primary MgCl2.3.3EtOH adduct (PCT1) was prepared by melt quenching method and then submitted into a programmed thermal dealcoholation project using a fluidized bed reactor. During thermal dealcoholation program, differen...
Selective production of light olefins from methanol over desilicated highly siliceous ZSM-5 nanocatalysts
Highly siliceous ZSM-5 nanocatalysts can dehydrate methanol to a wide range of hydrocarbons. In this study, the development of hierarchical H-ZSM-5 nanocatalysts (Si/Al=200) were reported for the methanol-toolefins (MTO)...
Biodegradation of PP films modified with organic pro-degradant: natural ageing and biodegradation in soil in respirometric test
In this study, PP films were modified with an organic pro-degradant in different concentrations (1, 2 and 3 wt.%), exposed in the first step of degradation to natural ageing for 100 days followed by biodegradation in sim...
Addition of a second alcohol in magnesium ethoxide synthesis as a way to vary the pore architecture of Ziegler-Natta catalysts
In Ziegler-Natta olefin polymerization, the pore architecture of catalysts plays a crucial role in catalytic performances and polymer properties. While the type of preparation routes (such as chemical reaction and soluti...