STUDY OF SELECTED USABLE PROPERTIES OF THE TOP LAYERS OF WELD OVERLAYS PRODUCED BY LASER TECHNOLOGY FOR APPLICATIONS IN THE POWER INDUSTRY
Journal Title: Tribologia - Year 2018, Vol 277, Issue 1
Abstract
The paper presents the results of laboratory tests of test specimens produced by multi-layer laser padding alloy Stellit Co-6 powder on a substrate with heat-treated X22CrMoV12-1 alloy steel. Multilayer laser padding was performed on a TRUMPF TruLaser Cell 3008. The formed weld overlays surface was studied using an optical microscope. Selected usable properties, such as surface topography, microstructure, hardness and erosion resistance were studied. During the analysis, areas of cross-sections test specimens after multilayer laser padded, in the connection zone of the substrate material with weld overlay, no cracks and no discontinuities in weld overlay were found in the substrate. As a result of conducted experiments, regular, repetitive weld overlays with characteristic directional crystallization were obtained. A microstructure with different growth directions with respect to the surface of the substrate shaped coniferous dendrites was obtained. The hardness of the weld overlays was in the range from 420 to 620 HV0.1, and in the heat affected zone, in the range of 320 to 420 HV0.1. Significant increases in erosion resistance of the surface layer of Stellite type Co-6 weld overlay produced by laser in comparison with the parent material after hardening were found.<br/><br/>
Authors and Affiliations
Wojciech NAPADŁEK, Adam WOŹNIAK
Keywords
Related Articles
- EP ID EP346182
- DOI 10.5604/01.3001.0011.9932
- Views 59
- Downloads 0
THE INFLUENCE OF SPRAY LUBRICATION OF AN OPEN GEAR TRANSMISSION ON THE TOOTH WEAR AND TRANSMISSION EFFICIENCY
The article covers the issues of the influence of the type of lubrication on the tribological wear and operational reliability of open gears in the propulsion system of ball mills and rotary kilns. The influence of the t...
THE INFLUENCE OF THE REPOSE ANGLE AND POROSITY OF GRANULAR PLANT MATERIALS ON THE ANGLE OF INTERNAL FRICTION AND COHESION
Internal friction in granular plant materials is a very complex phenomenon. This is due to a vast number of factors that determine the behaviour of these materials. This article looks at exploring the impact of porosity,...
Wzdłużne pole magnetyczne w szczelinie poprzecznego łożyska ślizgowego
W pracy autorzy przedstawiają analityczno-numeryczną metodę wyznaczania składowych wektora natężenia pola magnetycznego w szczelinie walcowego łożyska ślizgowego. Zagadnienie to staje się istotne, gdy jako czynnik smarow...
Warstwy węglikowe wytwarzane w procesie chromowania próżniowego na powierzchni stali pokrytej stopami niklu z pierwiastkami węglikotwórczymi
W pracy omówiono wyniki badań warstw duplex typu CrC+(Ni-Mo), CrC+(Ni-W) oraz CrC+Ni, wytwarzanych na powierzchni stali narzędziowej w procesie chromowania próżniowego połączonym z obróbką galwaniczną. Przeprowadzono pom...
AlSi ALLOYS FOR MAGNETRON DEPOSITION OF THE COATINGS ON CAR EXHAUST MUFFERS – FORECAST OF TECHNOLOGICAL WEAR
In the production of car exhaust system parts, for protection against corrosion and high-temperature oxidation, alumina and AlSi alloy hot-dip coatings are currently especially effective. The authors of this study are co...