Study on fl ame retardant ABS
Journal Title: Materials Science: Materials Review - Year 2017, Vol 1, Issue 1
Abstract
Flame-retardant ABS resin was prepared by adding flame retardant, toughening agent and dispersing silicone oil with acrylonitrile-butadiene-styrene resin (ABS, grade 0215 A) as raw material. The results showed that in the ABS resin, flame retardant with tetrabromobisphenol A and antimony trioxide as the composite system (the mass ratio of 2:1) was added. When the bromine content of the system was more than 10%, the flame retardant ABS meets the requirements of UL 94 V-0. The best toughening agent for flame retardant ABS resin is ABS graft powder. When the amount of flame retardant ABS is 9% ~ 19% (mass fraction) Strength of 150-200 J / m; in the same formula and operating conditions, brominated alkylene oxide as flame retardant prepared flame retardant ABS resin, the weather resistance is better than tetrabromobisphenol A as flame retardant The Composite expansion flame retardant and coated red phosphorus is an effective halogen-free flame retardant.
Authors and Affiliations
Xiaonan Lin,Wenmin Feng,Liangzhu Xu
Keywords
Related Articles
- EP ID EP679050
- DOI -
- Views 170
- Downloads 0
Cooling Rate, Hardness and Microstructure of Aluminum Cast Alloys
This experiment investigated the cooling curve behavior, hardness and microstructure of two aluminum alloys produced by casting process. There are Al-1.37Zn-1.19Si and Al-1.66Si-1.35Zn derived from melting and alloying a...
Quasi-particle Contribution in Thermal Expansion and Thermal Conductivity in Metals
In this paper the modified Landau theory of Fermi Liquids was used to compute the thermal expansion and thermal conductivity of quasi-particles in metals. The result revealed that as temperature increases the thermal exp...
Assessment of the Effect of Hydrolysed Starch Graft Copolymers Application on Soil Nutrient (Phosphorus and Nitrogen) Retention
The effects of the application of the graft copolymers (Hydrolyzed starch-g-polyacrylonitrile (HSPAN) and Hydrolyzed starch-g-polyacrylic acid (HSPAA)) on the nitrogen (N) and phosphorus (P) retention capacity of soil wa...
Behavior of Cast {TI or Ta}-Containing Alloys Based on Nickel and/or Cobalt in High Temperature Oxidation: Effect of the Ni/Co Ratio
Many of the cast superalloys chosen for specific applications at high temperatures, such as tools devoted for shaping molten glass, are based on nickel or cobalt. They contain chromium and carbon to achieve good resistan...
Study on the influence of the springback on the hole expansion ratio characterization
Material formability has become one of the main problems, together with the springback, when stamping high added-value components for the automotive industry. The pursuit of weight reduction has led to higher strength al...