The attempt at evaluation of the ADI microstructure with the use of the image analysis
Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 2
Abstract
In this work the attempt at quantitative evaluation of the microstructure of ADI cast iron matrix has been made. The automatic analysis of the image of the microstructure of austempered spheroidal cast iron has been used for the evaluation. The treatment variant was a two-phase austenitization. First phase was carried out at a temperature t = 950°C and after cooling to a temperature t ’ = 900°C. The isothermal process was carried out at a temperature tpi = 300 and 400°C for 8÷64 min. Ordinary cast iron was austempered. After it the microstructure images were recorded and subjected to automatic image analysis with the use of the NIS ELEMENTS 3,0 AR software.
Authors and Affiliations
T. Giętka, S. Dymski
Keywords
Related Articles
- EP ID EP72249
- DOI -
- Views 107
- Downloads 0
The assessment of hot cracking susceptibility of ferritic-austenitic cast iron
An inspiration to the research work has arisen from the problems related to cracking of massive castings made of ferritic-austenitic cast steel. The shape and the character of crack trajectories indicate that they are ho...
Tribological resistance of high speed steel HS 6-5-2 remelted with electric arc
The intensity of tribological wear of the high speed steel HS 6-5-2 remelted with the GTAW method has been compared to the heat treatment steel in a conventional way. Moreover, the types of the wear appeared during the f...
Selected parameters of moulding sands for designing quality control systems
One of the modern methods of production optimisation are artificial neural networks. Neural networks owe their popularity to the fact that they are convenient tools, which can be utilised in a wide scope of problems. The...
Three-dimensional numerical model of solidification with motion of the liquid phase
The paper presents numerical modeling of solidification process with convective motion of the liquid phase, generated both in the liquid and mushy zones. The transition region between the areas filled with liquid and sol...
The effect of casting porosities on cavitational erosion of intermetallic alloy FeAl36
The machinery and equipment elements operating in a turbulent fluid flow, are exposed to destruction as a result of the impact of the cavitation, corrosion and abrasion processes, among which are hardest to minimize the...