The Effect of Sintering Program on the Compressive Strength of Zirconia Copings
Journal Title: Journal of Dentistry, Shiraz University of Medical Sciences - Year 2018, Vol 19, Issue 3
Abstract
Statement of the Problem: Considering the limitations of conventional sintering of zirconium oxide (ZrO2) copings, shortening the sintering time can be proposed as an alternative method for making the copings. Purpose: This study aimed to assess the effects of sintering time on compressive strength of Yttria Tetragonal Zirconia Polycrystal (Y-TZP) copings. Materials and Method: Thirty copings of pre-sintered 3Y-TZP blanks were milled and sintered in a special furnace for three different durations (n=10 per group). The sintering time was 1 h 15 min for IPS e.max ZirCAD, 4 h 20 min for Speed ZrO2, and 7 h 20 min for the conventional ZrO2 group. The specimens were cemented on the brass dies by using conventional glass ionomer cement. The copings were vertically loaded until fracture by using a universal testing machine. The data were analyzed through one-way analysis of variance (ANOVA) and post hoc test to compare the mean differences of compressive strength yielded in three study groups (α=0.05). Results: The mean ± SD of compressive strength value was (3617 ± 543.54) N for IPS-e.maxZirCAD group, (2663 ± 508.11) N for Speed ZrO2 group, and (1662± 466.71 N) for conventional ZrO2 group. There were statistically significant differences among compressive strength values of the tested groups (p< 0.05). The highest compressive strength values were obtained from the IPS e.max ZirCAD group. Conclusion: Within the limitations of this in vitro study, it can be concluded that compressive strength of the zirconia copings is affected by the sintering time. High compressive strength of zirconia copings can be obtained by shortening the sintering time.
Authors and Affiliations
Azita Tehranchi, Farnaz Younessian, Vida Fadaei, Fariba Arabgol, Armin Shirvani
Keywords
Related Articles
- EP ID EP369540
- DOI -
- Views 72
- Downloads 0
Comparison between Glenoid Fossa Roof Thickness in TMD and non-TMD Patients, a CBCT Study
Statement of the Problem: Various pathologic conditions can affect the thickness of the roof of glenoid fossa (RGF). The relationship between the RGF thickness and temporomandibular joint disorder (TMD) is not explicitly...
The Effect of Disinfection with Chlorhexidine on the Shear Bond Strength of Equia Resin-Modified Glass Ionomer Cement to Dentin in Permanent Teeth after Two Thermocycling Protocols
Statement of the Problem: There are some concerns regarding the effect of chlorhexidine (CHX) applied for cavity disinfection on the bond strength of adhesive restorations to dentin. Purpose: This study sought to assess...
The Protective Role of Front-Closed and Front-Open Gowns Against Staphylococcus Aureus Contamination of Dental Students before and after Restorative Treatments
Statement of the Problem: Due to the close contact with patients during dental treatments, dentists and those affiliated to the dental profession are at higher risk for various infections. Infection prevention in dentist...
Comparative Evaluation of Penetration Ability of Three Pit and Fissure Sealants and Their Relationship with Fissure Patterns
Statement of the Problem: Pit and fissure sealant placement is considered as an effective modality for prevention of caries on occlusal surfaces. Penetration, retention and lateral wall adaptation are the key factors in...
Demographic Evaluation of Oro-Dental Self-Injury for Insurance Deception; Evaluation of the Cases Referred to Shiraz Forensic Medicine Center
Statement of the Problem: Nonsuicidal self-inflicted injuries are socially unacceptable and may cause mild to severe damages. Purpose: This study aimed to evaluate the demographic features of the subjects with orodental...