THE INFLUENCE OF SOLUTION TREATMENT ON THE STRUCTURE AND MECHANICAL AND TRIBOLOGICAL PROPERTIES OF MAGNESIUM ALLOY WE54
Journal Title: Tribologia - Year 2016, Vol 267, Issue 3
Abstract
The paper presents the influence of solution treatment on the mechanical and tribological properties of the WE54 magnesium alloy. The investigated alloy was solution treated at a temperature of 545oC for 8 hours and cooled in ice water (0oC), in room temperature water (20oC), and in hot water (95oC). Depending on the applied solution treatment parameters, a diversified decrease in hardness and Young's modulus was obtained. The lowest values of hardness H and modulus E were obtained when cooling in ice water. Abrasive wear of alloy WE54 was tested using a ball-on-disc tribometer (with a ZrO2 ball). The tests have shown more than a threefold reduction in the volumetric wear and a twofold reduction in the linear wear, as well as favourable changes of the friction coefficient (a 20% decrease) as compared to the material in the as-received condition.<br/><br/>
Authors and Affiliations
Adam BARYLSKI, Krzysztof ANIOŁEK, Michał DWORAK
Keywords
Related Articles
- EP ID EP246189
- DOI 10.5604/01.3001.0010.7289
- Views 51
- Downloads 0
Wpływ dodatków smarnych na wybrane właściwości reologiczne
W pracy przedstawiono wyniki badania wpływu dodatków smarnych na właściwości reologiczne smarów. Badaniom poddano smar mineralny i syntetyczny, zawierający zróżnicowaną ilość dodatków: PTFE, talku i estrów kwasów tłuszcz...
TARCIE STATYCZNE W ODWRÓCONYCH PARACH ŚLIZGOWYCH METAL–ELASTOMER
Współpraca ślizgowa materiałów o różnych twardościach (odkształcalności), np. materiał polimerowy współpracujący z materiałem metalicznym, występuje w elementach maszyn w jednym z dwóch następujących wariantów: para pros...
TRIBOLOGICAL CHARACTERIZATIONS OF CHROMIZED CARBIDE LAYERS PRODUCED BY THE PACK POWDER METHOD AT LOW PRESSURE
Diffusion chromizing of tool steel was investigated using a powder method modified by the use of low pressure during the process for the avoidance of the oxidation of the batch. The processes were performed in a chromium...
INFLUENCE OF PAD GEOMETRY MODIFICATION ON THE PERFORMANCE OF THRUST BEARINGS LUBRICATED WITH MAGNETORHEOLOGICAL FLUID
Magnetic fluids belong to the class of controllable materials. The influence of magnetic fields on this type of substance results in a change in its internal structure and an almost immediate change in its rheological pr...
BADANIA WPŁYWU SIŁ TARCIA NA PRZENOSZENIE DRGAŃ GRUNTU NA RURĘ GAZOCIĄGU
W artykule przedstawiono wpływ wartości sił tarcia w kontakcie rury gazociągu z obsypką piaskową na przenoszenie drgań gruntu na badany odcinek rury. Przeprowadzono eksperymenty poligonowe, w trakcie których standardowo...