THE INFLUENCE OF THE TEMPERATURE AND ANODIC CURRENT ON THE CHANGES OF TRIBOLOGICAL PROPERTIES OF AL2O3/WS2 – PEEK/BG SLIDING COUPLE
Journal Title: Tribologia - Year 2010, Vol 231, Issue 3
Abstract
The paper describes the tribological behaviours of a sliding pair of Al2O3/WS2 layers – PEEK/BG material. The analysis of the results consists in determining the friction coefficient for the pair, stereometric measurements taken before and after tribological test, and also the intensity of PEEK/BG wear. The aim of this article is to determinate the influence of temperature and electric anodic current density used during hard anoding treatment in SFS electrolyte. The result obtained allow one to select a very best terms of technological treatment in order to get Al2O3/WS2 oxide layers that can be used in kinematic sliding pairs.<br/><br/>
Authors and Affiliations
Joanna Korzekwa, Władysław Skoneczny
Keywords
Related Articles
- EP ID EP517310
- DOI -
- Views 37
- Downloads 0
TRIBOLOGICAL PROPERTIES OF N-ALCOHOLS, N-ALKYLPHENYLS AND GLYCOLS ALKOXY DITHIOPHOSPHATES IN FRICTION CONTACTS: STEEL–STEEL, AL2O3–AL2O3 AND STEEL–AL2O3
The zinc di-n-alkyko(arylo)ethoxyditiophosphates, a new class of organodithio- phosphorous compounds(ZEDPs) with low phosphorous, low ash contents and high thermal stability have been prepared, they are very good AW/EP a...
ZNACZENIE BŁĘDÓW USTAWIENIA OPRAW ŁOŻYSKOWYCH WAŁU TRZYPODPOROWEGO DLA TRWAŁOŚCI ŁOŻYSKOWANIA
W układach napędowych maszyn i urządzeń bardzo często występują długie wały napędowe, które wymagają osadzenia na kilku podporach. Dlatego też ustalenie wpływu dokładności wykonania i montażu oraz warunków pracy łożysk n...
THE APPLICATION OF THE ROUGH SETS THEORY FOR THE ANALYSIS OF SURFACE ROUGHNESS FACTORS INFLUENCING SURFACE FATIGUE LIFE
Fatigue wear is a kind of wear when the local loss of cohesion and subsequent material decrements are caused by material fatigue in the effect of cyclic action of contact stresses in surface layers of joint friction elem...
ABRASIVE WEAR RESISTANCE OF METAL-POLYMER COMPOSITES
The paper presents the results of resistance to abrasive wear of various material junctions. The purpose of this study was to assess the potential application of composite materials for the regeneration of friction pairs...
WŁAŚCIWOŚCI TRIBOLOGICZNE STALI ŁOŻYSKOWEJ PO OBRÓBCE HYBRYDOWEJ, ŁĄCZĄCEJ DYFUZYJNE CHROMOWANIE Z METODĄ PVD
Przedmiot badań w niniejszej pracy stanowiła modyfikacja budowy warstw chromowanych na stali łożyskowej przez połączenie chromowania dyfuzyjnego z następną obróbką, osadzaniem azotku chromu metodą PVD, przeprowadzana dla...