TRIBOLOGICAL PROPERTIES OF CAST IRON EN-GJSFP-500-7 AFTER A BURNISHING PROCESS MODIFIED BY EXPLORATION PREPARATIONS BASED ON SOLID LUBRICANT AND CHEMICAL ACTION
Journal Title: Tribologia - Year 2013, Vol 250, Issue 4
Abstract
In the paper, the results of research on the base machine oil SN-150 and the exploitative preparations R-2000 (preparation on the basis of soft metals) and Motor LIFE (preparation using chemical actions) influence on the tribological properties and stereometric state of cast iron EN-GJSFP- -500-7 after a burnishing process. For comparative purposes, dry burnishing was also performed. These investigations were executed on tester T-05 (a roll – the block type tester). The main aim was to establish how the exploitative preparations R-2000 and MotorLIFE influence the surface layer state after the burnishing process. The waste investigations of the burnished surface were realized. Conducted investigations, the obtained results, and their analysis confirm the positive influence of the exploitative preparation MotorLIFE on tribological properties as well as the roughness parameters improvement in relation to the samples of dry burnishing, base machine oil SN-150, and exploitative preparation R-2000.
Authors and Affiliations
Albert Lewandowski
Keywords
Related Articles
- EP ID EP270059
- DOI -
- Views 29
- Downloads 0
RELATION BETWEEN SHEAR STRESS AND SHEARING TIME IN SELECTED LUBRICANT COMPOSITIONS
The paper presents the results of studies of the influence of fillers introduced into lubricating greases on changes in values of shear stresses in resulting lubricant compositions. These fillers were powders of graphite...
THE TRIBOLOGICAL PROPERTIES OF METAL-POLYMER COMPOSITES IN DRY CONDITIONS
In the paper, the results of tribological tests of metal-polymer composites and bronze pair without external lubrication were presented. The friction and wear tests were performed using the composites with solid lubrican...
Charakterystyki tribologiczne materiałów przeznaczonych na elementy łożysk foliowych
W artykule przedstawiono wyniki badań tribologicznych materiałów przeznaczonych na elementy wysokoobrotowego łożyska foliowego. Przebadano dwa rodzaje folii wykonanych przez Instytut Technologii Materiałów Elektronicznyc...
Badania tribologiczne powłok ceramicznych natryskiwanych plazmowo
Części współczesnych maszyn często wymagają ochrony powierzchni roboczych przed działaniem korozyjnym, zużyciem oraz doraźnymi uszkodzeniami mechanicznymi. Do tego wykorzystuje się powłoki nanoszone na powierzchnie roboc...
Modelowanie i badania eksperymentalne pękania cienkich powłok ceramicznych i węglowych
Praca zawiera analizę deformacji i naprężeń prowadzących do niszczenia układów powłoka–podłoże przez odkształcenia plastyczne podłoża i pękanie twardych powłok. Do analizy wykorzystano obliczenia numeryczne metodą elemen...