Use of fluidized bed reactor in 2,6-dimethylphenol synthesis
Journal Title: CHEMIK nauka-technika-rynek - Year 2014, Vol 68, Issue 5
Abstract
Research works were focused on obtaining and testing of catalysts for 2,6-dimethylphenol synthesis that could be used as fluidized bed. Silicon oxide was synthesized, on which subsequently various variants of iron (III), magnesium (II), chrome (III) and copper (II) oxides were deposited. Moreover, catalyst TZC-3/1 produced by Grupa Azoty SA was tested. Silicon oxide with deposited magnesium oxide allowed almost 100% conversion of phenol at 733K with selectivity towards 2,6-dimethylphenol equal to 60%. Similar degree of conversion for phenol was obtained for industrial catalyst TZC-3/1, but its selectivity towards 2,6-dimethylphenol was equal to 90%. Experimental results indicate that the best one among examined catalyst is the industrial catalyst TZC-3/1 that allows obtaining best results at lowest temperature.
Authors and Affiliations
D. Jamanek, M. Zielecka, Z. Wielgosz, K. Cyruchin, B. Kępska, A. Górska, J. Krakowiak, P. Baran
Keywords
Related Articles
- EP ID EP115888
- DOI -
- Views 68
- Downloads 0
Carbon capture, wiedzieć jak najwięcej – nasz wspólny cel
Największymi wyzwaniami dla procesu aminowego usuwania CO2 ze spalin z konwencjonalnych elektrowni węglowych, jest ograniczenie energii wymaganej do regeneracji roztworu oraz określenie barier technologicznych stojących...
The photostability of poly (lactic acid) / polyacrylates composites as new materials for the packaging industry
Composite films of poly (lactic acid) (PLA) with polyacrylates of varying composition and proportions of the components were obtained by photochemical reaction. The aim of the study was to investigate composites photo...
Nanonośniki jako nowoczesne transportery w kontrolowanym dostarczaniu leków
W systemie kontrolowanego dostarczania leków na poziomie nanocząstek (NP) wykorzystuje się różne ugrupowania, w tym polimery, materiały węglowe oraz nanocząstki magnetyczne. Wymienione związki, występują w postaci proste...
FT-IR studies of zeolites from different structural groups
The paper presents the results of FT-IR studies of zeolites (mainly natural) belonging to the seven major structural groups. Interpretation of vibrational spectra has been based on the identification of the bands associa...
Możliwości analityczne generowania lotnych wodorków w technice optycznej spektrometrii emisyjnej (HG-ICP-OES)
Przedstawiono możliwości analityczne oznaczania arsenu oraz innych pierwiastków tworzących lotne wodorki w materiałach środowiskowych, z uwzględnieniem technik generowania wodorków. Na podstawie doniesień liter...