ANALYSIS OF FRACTURE AND WEAR RESISTANCE OF ZrN COATINGS
Journal Title: Tribologia - Year 2017, Vol 273, Issue 3
Abstract
The article presents the results of mechanical and tribological studies of ZrN coatings that allowed the determination of their hardness, elasticity modulus, and scratch and wear resistance. Tests were carried out for 1, 1.4, and 2 μm thick ZrN coatings deposited on X5CrNi18-10 austenitic steel substrates by PVD technology. Hardness and Young's modulus of coatings, evaluated by nanoindentation, were within the 26–32 GPa, and 330–360 GPa ranges, respectively. Analysis of the adhesion of the coating to the substrate was carried out based on the results of the scratch test. The highest critical load values of LC1 and LC2 were measured for the 1.4 μm thick coating. Tribological tests performed using a ball-on-disc tribotester showed that the wear resistance increases with coating thickness. This was accompanied by a reduction of the coefficient of friction from 0.22 to 0.17.
Authors and Affiliations
Kinga CHRONOWSKA-PRZYWARA, Marcin KOT
Keywords
Related Articles
- EP ID EP239463
- DOI -
- Views 71
- Downloads 0
Charakterystyki tribologiczne warstwy Al2O3 modyfikowanej grafitem w skojarzeniu ślizgowym z kompozytami polimerowymi
W pracy przedstawiono właściwości tribologiczne warstw Al2O3 modyfikowanych grafitem. Ceramiczno-grafitowe warstwy powierzchniowe zostały wytworzone na stopie aluminium EN-AW 5251 technologią „duplex” oraz technologią be...
FUNCTION OF THE MENISCI IN THE LOAD TRANSFER WITHIN THE KNEE JOINT
The aim of the study was to conduct strength analysis of a knee joint in order to experimentally determine the destructive fatigue loading under the conditions of cyclic compression. Animal joints were used as the study...
THE EFFECT OF NANOCRYSTALLINE LAYERS ON THE WEAR RESISTANCE OF GREY CAST IRON DURING FRICTION IN AN OIL-ABRASIVE MEDIUM
Friction hardening is one of the surface hardening methods with the use of highly concentrated energy sources. In the “tool-treated surface” contact area, the surface layer of a metal is heated at a very high rate to pha...
WPŁYW TEKSTUROWANIA LASEROWEGO POWIERZCHNI NA TARCIE I ZUŻYWANIE PTFE PODCZAS WSPÓŁPRACY ZE STALĄ
Przedstawiono badania i analizę zużycia PTFE podczas współpracy ze stalą. Powierzchnię elementów stalowych poddano teksturowaniu laserowemu. Na powierzchnię elementów stalowych naniesione zostały 3 różne wzory struktur....
ANALIZA WPŁYWU PARAMETRÓW TECHNOLOGII FDM NA WŁAŚCIWOŚCI TRIBOLOGICZNE
Przedstawiono wyniki badań tribologicznych modeli próbek wykonanych w technologii FDM osadzania topionego materiału. Próbki w kształcie pierścieni wykonane zostały z materiału ABS P430 przy wykorzystaniu maszyny Dimensio...