Analysis of the Inconel 600 alloy destruction process in the surrounding of oxygen, nitrogen and hydrogen
Journal Title: Archiwum Odlewnictwa - Year 2010, Vol 10, Issue 3
Abstract
This paper presents results of research, which was targeted to define reasons of the short life of sieves made from a 0.8mm diameter wire of the INCONEL 600 alloy. It was noticed that when the sieves were used in the device for the nitrogen acid production there appeared a total loss of plastic properties of the wire. It was caused by the process of diffusion of oxygen, nitrogen and metal ions which was not stopped although the protective layer of the scale was produced. It resulted in the substantial decrease of the chromium contents (to ca 1.5%) and in oxidation of the grain boundary in the wire outer layer. The diffusion of nitrogen to the wire core caused in turn the precipitation of many Cr2N nitrides in the core.
Authors and Affiliations
M. Gajewski, J. Kasińska, R. Mola
Keywords
Related Articles
- EP ID EP72128
- DOI -
- Views 92
- Downloads 0
Model of knowledge representation about materials in the form of a relational database for CAPCAST system
This study is related with one of the components of a hybrid decision support system called CAPCAST, implemented under a research project conducted by WIMIIP AGH. It is a model of knowledge representation about materials...
Application of time-series analysis for prediction of molding sand properties in production cycle
Time-series analysis is characterized, as a data mining tool which facilitates understanding nature of manufacturing processes and permits prediction of future values of the process parameters or production results on th...
Reclaimability of the spent sand mixture – sand with bentonite – sand with furfuryl resin
Introduction of new binding materials and new technologies of their hardening in casting moulds and cores production requires the application of reclamation methods adequate to their properties as well as special devices...
Corrosion behaviour of the AlSi6Cu4 alloy and cast AlSi6Cu4-graphite particles composite
The corrosion behaviour of the AlSi6Cu4 alloy as a composite matrix and of composites with 8% vol. of graphite particles was investigated. The corrosion experiments were performed over a range of elevated temperatures an...
Kinetics of hardening of ceramic layers applied in the investment patterns method
The work presents results of investigations of a hardening rate of ceramic moulds applied in investment patterns method. During the studies, the original method based on the ultrasonic technique, and a novel testing rout...