CHOSEN PROPERTIES OF SANDWICH MATERIAL Ti-304 STAINLESS STEEL AFTER EXPLOSIVE WELDING
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2011, Vol 18, Issue 1
Abstract
The work deals with evaluation of joint of stainless steel 304 SS (sheet) and commercially pure Ti both after welding explosion and followed-up annealing at 600°C/1.5h/air. The bonding line shows sinusoidal character with curls in crest unlike the trough of the sine curve. The heat treatment does not change the character of the interface. In work amplitude, wave length and the interface thickness were measured. Thickness of compressed cladded matrix of Ti was measured in area of crests and troughs. In crest of joint melted zones were studied, where complex oxides and intermetallic phases were revealed
Authors and Affiliations
Dmytro Ostroushko, Eva Mazancová
Keywords
Related Articles
- EP ID EP145133
- DOI -
- Views 116
- Downloads 0
KINETICS OF HARDNESS CHANGES DURING AGE-HARDENING OF SILUMIN
Simple phenomenological description of age-hardening kinetics of supersaturated solid solution is presented using the sum of exponential functions with negative arguments containing rate constants, for whose temperature...
Improvement of the wear behaviour of highly-loaded components and tools by multi-combined surface treatment
These multi-combined surface treatments lead to a significant improvement in load-supporting capacity. Critical load values of cohesive failure measured by scratch tests are tripled when compared to the individual treatm...
STATICAL EXPERIMENTS OF TIRE AS COMPLEX LONG-FIBRE COMPOSITE FOR OBTAINING MATERIAL PARAMETERS AND DEFORMATION CHARACTERISTICS
The article deals with the statical experiments of tires for obtaining material parameters and deformation characteristics by tensile testing machine and also special statical testing tire machine. The tires consist of p...
COMPUTER CONTROLLED EXPERIMENTAL DEVICE FOR INVESTIGATIONS OF TRIBOLOGICAL INFLUENCES IN SHEET METAL FORMING
Sheet metal forming, especially deep drawing process is influenced by many factors. Blank holding force and drawbead displacement are two of them that can be controlled during the forming process. For this purpose, an e...
MICROSTRUCTURAL STABILITY OF Ti-46Al-8Ta DURING CREEP
The effect of long-term creep exposure on the microstructure stability of a new cast air-hardenable intermetallic alloy with nominal chemical composition Ti-46Al-8Ta (at .%) was studied. Constat load creep test were per...