Composition Design and Microstructure Analysis of Titanium Microalloyed New Die Steel

Journal Title: 河南科技大学学报(自然科学版) - Year 2019, Vol 40, Issue 5

Abstract

JMatPro software was used to simulate the H13 steel with different mass fraction Ti. According to the calculation results, the new mold steel with different Ti mass fraction was designed. The mechanical properties and microstructure of H13 steel with different Ti mass fraction after heat treatment were analyzed. The results show that it is reasonable to add Ti element mass fraction less than 0.600%. The tensile strength, hardness and plasticity of H13 steel containing trace Ti increase first and then decrease with the increasing of Ti content after quenching and tempering at room temperature. The performance achieves the best when the mass fraction of Ti is 0.127%. The maximum tensile strength and hardness at room temperature are 1 788 MPa and 51.5 HRC, respectively. Compared with H13 steel without Ti, it increases 264 MPa and 3. 7HRC respectively, and the reduction of area increases from 35.0% to 47.0%. The quenching and tempering micro structure of H13 steel with Ti mass fraction of 0%, 0.044% and 0.127% respectively is a mixture micro structure of tempered sorbite and tempered troostite. The quenching and tempering micro structure of H13 steel with Ti mass fraction of 0.325% and 0.536% is tempered sorbite.

Authors and Affiliations

Yongjian WANG, Yanmin ZHANG, Yaoli WANG, Kexing SONG, Yunfei WANG

Keywords

Related Articles

Size Effect of Glass Fiber Reinforced Plastic Confined Concrete Column

Three glass fiber reinforced plastic( GFRP) confined reinforced concrete columns and three unconfined reinforced concrete columns were tested and the finite element analysis was carried out on 15 specimens. The influence...

A Semi-supervised Canonical Correlation Analysis Algorithm Based on Deep Boltzmann Machine

To solve the problem that the canonical correlation analysis( CCA) algorithm was not adapted to the high level of correlation,through pattern classification,an improved algorithm was proposed based on semisupervised cano...

Design of Multi-channel Arbitrary Waveform Generator with Precision Phase Control

Multi-channel arbitrary waveform generator with extensible channel and high precision phase control was designed in order to meet the requirements of multi-channel waveform and phase. Based on the direct digital frequenc...

Design and Performance Analysis of Spiral Bevel Gear with Arc Constant-depth Tooth

In order to improve the diagonal phenomenon of gear pair, conventional spiral bevel gear tapered teeth was changed into constant-depth tooth with No. 0 cutter while milling. Based on local meshing principle of gears, too...

Effects of Environmentally Friendly Plasticizers on High and Low Temperature Performance of Natural Modified Asphalt

In order to explore the effects of different environmental plasticizers on the high and low temperature performance of different natural asphalts, the high and low temperature rheological properties of environmentally fr...

Download PDF file
  • EP ID EP594600
  • DOI 10.15926/j.cnki.issn1672-6871.2019.05.001
  • Views 87
  • Downloads 0

How To Cite

Yongjian WANG, Yanmin ZHANG, Yaoli WANG, Kexing SONG, Yunfei WANG (2019). Composition Design and Microstructure Analysis of Titanium Microalloyed New Die Steel. 河南科技大学学报(自然科学版), 40(5), 1-6. https://europub.co.uk./articles/-A-594600