Effect of ECAP process on structure and hardness of AlMg3 aluminium alloy
Journal Title: Archives of Materials Science and Engineering - Year 2017, Vol 2, Issue 84
Abstract
Purpose: In the present study, the effect of ECAP die and number of ECAP pressings on the structure evolution and hardness of AlMg3 aluminium alloy was investigated. Design/methodology/approach: Commercial AlMg3 aluminium alloy in the as-cast condition was processed by Equal Channel Angular Pressing method through route A using two different ECAP dies – conventional and modified with additional twist angle. Samples were processed at ambient temperature up to four passes. The investigation was carried out at ambient temperature. Two different ECAP dies were used to investigate the effect of design modification on the possibility of grain refinement to sub-micrometer size. Findings: The experimental results showed that the modification of ECAP die provides to additional grain refinement and introduces a greater amount of plastic strain into the material which results in greater increase in the properties of the investigated material. Research limitations/implications: The presented investigation results were carried out on samples, not on final products. Practical implications: Current research is moving towards to develop high strength materials with increased mechanical properties and refined microstructure that are known as ultra-fine-grained materials, compared to well-known with coarse-grained microstructure. Originality/value: The paper focuses on the investigation of microstructure evolution using mainly polarised light microscopy that reveals shear, micro-shear and slip bands that refine the microstructure of aluminium alloys. In addition, to evaluate the grain size of as ECAPed specimen, EBSD investigation was carried out.
Authors and Affiliations
P. Snopiński, T. Tański, O. Hilšer, A. Lubos
Keywords
Related Articles
- EP ID EP189617
- DOI 10.5604/01.3001.0010.0982
- Views 84
- Downloads 0
Influence of plastic deformation temperature on the structure and mechanical properties of low-alloy copper alloys with Co, Ni and B
Purpose: This work presents the influence of chemical composition and plastic deformation temperature of CuCoNi and CuCoNiB as well as CuCo2 and CuCo2B alloys on the structure, mechanical properties and, especially on th...
Microstructure and mechanical properties of HR3C austenitic steel after service
Purpose: The purpose of the investigations was to determine changes in the microstructureand mechanical properties of HR3C creep resisting austenitic steel after service.Design/methodology/approach: The investigations we...
Combined thermal, microstructural and microchemical analysis of solidification of Al25Si3Cu alloy
Purpose: This paper present thermal and microstructural and microchemical analyses were conducted on the unmodified experimental alloy Al20Si3Cu (B390.1) solidified in the High Temperature Universal Metallurgical Simulat...
Ultrasonic method of quality control for textile materials
Purpose: The ultrasonic amplitude method for controlling the surface texture density of textile materials was first studied and used. Design/methodology/approach: For the first time, the surface texture density has been...
Chromous capacities of ferrochromium and matte smelting slags
Purpose: of this paper is to extend the slag capacity concept to sparingly soluble cationic species encountered for example in matte smelting and ferrochromium processing in terms of chromous capacities. Design/methodolo...