Effect of Microstructure on the Compressive Mechanical Properties of Ti-20Zr-6.5Al-4V Alloy
Journal Title: Materials Science-Medžiagotyra - Year 2019, Vol 25, Issue 1
Abstract
The effect of microstructure on the mechanical properties of Ti-20Zr-6.5Al-4V alloy after solution and aging treatment was investigated by compression tests. The results showed that the microstructure was consisted of a duplex phase αʺ + β structure after solution treatment. With increasing solution treatment temperature, the size of β phase grain increased and the amount of αʺ phase decreased. The ultimate compressive strength and elongation decreased with increasing solution treatment temperature, while the yield strength increased. After aging-treatment at 700 ºC for 1.5 h, the microstructure consisted of a large amount of globular α phase, a little amount of fine acicular α phase and bulk β phase for the samples solution-treated at 850 ºC for 0.5 h. With increasing initial solution treatment temperature, the amount of globular α phase and bulk β phase decreased, however, the amount and size of acicular α phase increased after aging treatment. The ultimate compressive strength and elongation decreased with increasing initial solution treatment temperature, whereas the yield strength firstly increased, and then slightly decreased.
Authors and Affiliations
Yuanbiao TAN, Jingli DUAN, Wenchang LIU, Song XIANG, Fei ZHAO, Yilong LIANG
Keywords
Related Articles
- EP ID EP452515
- DOI 10.5755/j01.ms.25.1.18737
- Views 62
- Downloads 0
Effect of Annealing Temperature on Structural, Morphological, Optical and Electrical Properties of Spray Deposited V2O5 Thin Films
Nanostructured vanadium pentoxide (V2O5) thin films have been deposited by a simple and cost-effective spray pyrolysis technique (SPT) at substrate temperature 300 °C and post annealed at atmospheric conditions in the te...
Grain Growth Model of Ultra-Fine Grain AZ80 Magnesium Alloy Multi-Directionally Forged During the Isothermal Heating Process
This paper takes the ultra-fine grain AZ80 magnesium alloy multi-directionally forged as the research object. We observe its heating behavior at 673 K with an optical microscope, analyze the grain size distribution, and...
Evaluation of the Effect of Thermo-mechanical Treatment on the Resistance of Commercial OSB to Decay Fungi
The chemical treatment of wood has been widely used in combating rot fungi. However, it’s a process that involves the insertion of chemical agents, which are subject to leaching when exposed to weathering. In this contex...
Enhanced Magnetic Squareness in Manganese-Bismuth Mechanical Alloys Incorporating Magnesium Oxide
Manganese-bismuth (MnBi) mechanical alloys have been under development for novel permanent magnets without rare-earth elements. The ball-milling of bismuth (III) oxide and manganese powders in this work leads to soft mag...
Effect of Microstructure on the Compressive Mechanical Properties of Ti-20Zr-6.5Al-4V Alloy
The effect of microstructure on the mechanical properties of Ti-20Zr-6.5Al-4V alloy after solution and aging treatment was investigated by compression tests. The results showed that the microstructure was consisted of a...