EVALUATION OF MICROSTRUCTURAL STABILITY OF DISSIMILAR WELD JOINTS
Journal Title: Materials Engineering - Materialove inzinierstvo (MEMI) - Year 2011, Vol 18, Issue 4
Abstract
The microstructural changes occurring in the weld joint P92/316Ti during his long-term exposure at high temperature were studied. In parallel to experiments were carried out calculations of phase equilibria for the base materials and the weld joint using the ThermoCalc software. Based on the experimental results and computational modeling results were evaluated a microstructural stability and the application of the base materials and the weld joint.
Authors and Affiliations
Pavel Sohaj
Keywords
Related Articles
- EP ID EP155526
- DOI -
- Views 111
- Downloads 0
STUDY ON PHYSICAL - MECHANICAL PROPERTIES OF ALKALI ACTIVATED MATERIALS BASED ON FLY ASH
Alkali activated materials are relatively new materials, thanks to their good mechanical, physical, thermal properties and at the same time environmental friendliness, they could be widely adopted in different fields. Th...
INTERNAL FRICTION USE IN MONITORING THE DEGRADATION PROCESSES IN A MATERIAL
During the measurement of the fatigue life of material, the specimen undergoes large number of stress cycles. While the observed number of cycles before failure is considered to be the most important result (often the on...
STRUCTURAL CHARACTERISTICS & DIELECTRIC PROPERTIES OF TANTALUM OXIDE DOPED BARIUM TITANATE BASED MATERIALS
In this research, the causal relationship between the dielectric properties and the structural characteristics of 0.5 & 1.0 mole % Ta2O5 doped BaTiO[sub]3[/sub] based ceramic materials were investigated under differe...
EVALUATION OF THE FLOW ACCELERATED CORROSION OF COPPER PIPES
Corrosion behavior of the Cu pipe system has been investigated by long term experiment. The two identical experimental systems were made and fulfilled by the solution of 3 % NaCl. The work medium in the first system was...
COMPUTER CONTROLLED EXPERIMENTAL DEVICE FOR INVESTIGATIONS OF TRIBOLOGICAL INFLUENCES IN SHEET METAL FORMING
Sheet metal forming, especially deep drawing process is influenced by many factors. Blank holding force and drawbead displacement are two of them that can be controlled during the forming process. For this purpose, an e...