Fracture mechanics analyses of the slip-side joggle regions of wing-leading-edge panels
Journal Title: Frattura ed Integrità Strutturale - Year 2011, Vol 5, Issue 15
Abstract
The Space Shuttle wing-leading edge consists of panels that are made of reinforced carbon-carbon. Coating spallation was observed near the slip-side region of the panels that experience extreme heating. To understand this phenomenon, a root-cause investigation was conducted. As part of that investigation, fracture mechanics analyses of the slip-side joggle regions of the hot panels were conducted. This paper presents an overview of the fracture mechanics analyses.
Authors and Affiliations
I. S. Raju, N. F. Knight, K. Song, D. R. Phillips
Keywords
Related Articles
- EP ID EP150454
- DOI 10.3221/IGF-ESIS.15.05
- Views 68
- Downloads 0
Natural minerals mixture for enhancing concrete compressive strength
The construction material quality is required to be improved in order to enhancing structure stability, optimizing construction cost and quality. The kaolin and bentonite have been mixed in equal quantity and treat...
Crack path and fracture surface modifications in cement composites
There is a tremendous increase in the use of high strength and high performance self-consolidating cementitious composites due to their superior workability and mechanical strengths. Cement composites are qua...
Analisi basata sugli sforzi locali della resistenza a fatica di giunzioni incollate di materiali compositi
Il lavoro prende spunto dai risultati di un’analisi sperimentale del comportamento a fatica di giunzioni incollate di materiali compositi laminati di elevato spessore formati da strati di unidirezionale e di tessuto di f...
Methodological developments in the field of structural integrity analyses of large scale reactor pressure vessels in Hungary
Buildings, structures and systems of large scale and high value (e.g. conventional and nuclear power plants, etc.) are designed for a certain, limited service lifetime. If the standards and guidelines of the time...
The numerical simulation of ceramic composites failure at axial compression
On the basis of the developed model of quasibrittle medium the brittle and quasibrittle failure of composite ceramic materials with zirconium dioxide matrix and various percentage of hardening particles of corundum...