High-cycle fatigue strength of a pultruded composite material
Journal Title: Frattura ed Integrità Strutturale - Year 2009, Vol 3, Issue 7
Abstract
Dealing with composites in polymeric matrix, the pultruded ones are among the more suitable for large production rates and volumes. For this reason, their use is increasing also in structural applications in civil and mechanical engineering. However, their use is still limited by the partial knowledge of their fatigue behaviour; in many applications it is, indeed, required a duration of many millions of cycles, while most of the data that can be found in literature refer to a maximum number of cycles equal to 3 millions. In this paper a pultruded composite used for manufacturing structural beams is considered and its mechanical behaviour characterized by means of static and high-cycle fatigue tests. The results allowed to determine the S-N curve of the material and to assess the existence of a fatigue limit. Observations at the scanning electronic microscope (SEM) allowed to evaluate the damage mechanisms involved in the static and fatigue failure of the material
Authors and Affiliations
C. Colombo, M. Guagliano, L. Vergani
Keywords
Related Articles
- EP ID EP97532
- DOI 10.3221/IGF-ESIS.07.05
- Views 85
- Downloads 0
Electrical resistivity and ultrasonic measurements during sequential fracture test of cementitious composite
Cracks in cover of reinforced and pre-stressed concrete structures significantly influence the ingress of deleterious species causing decrease in durability of these structures. The paper is focused on the effect...
Numerical modelling in non linear fracture mechanics
Some numerical studies of crack propagation are based on using constitutive models that account for damage evolution in the material. When a critical damage value has been reached in a material point, it is natural...
Experimental investigation of effect of specimen thickness on fracture toughness of Al-TiC composites
In this paper, the macro and micro-mechanical fracture behavior was studied for aluminum (Al6061) alloy matrix, reinforced with various proportions of TiC particles such as 3wt%, 5wt% and 7wt%. The Al6061-TiC...
Improvement of performance of ultra-high performance concrete based composite material added with nano materials
Ultra-high performance concrete (UHPC), a kind of composite material characterized by ultra high strength, high toughness and high durability. It has a wide application prospect in engineering practice. But t...
Limit analysis on FRP-strengthened RC members
Reinforced concrete (RC) members strengthened with externally bonded fiber-reinforced-polymer(FRP) plates are numerically investigated by a plasticity-based limit analysis approach. The key-concept of thepresent ap...