Investigation of composite coated Ti-C-N surfaces with ball-cratering test method
Journal Title: Carbon - Science and Technology - Year 2015, Vol 7, Issue 3
Abstract
We present the performance of dry sliding metal-metal wear performance of AISI SS410 and Ti-C-N coated specimens at room temperature. In this investigation, the ball cratering abrasive wear testing method was used with a various loads of 2N, 3N and 4N, with total sliding distance of 353.43 m and at a constant sliding speed of 0.3927 ms-1. In this testing machine the abrasive ball of high carbon steel with 750 HV at 100 g load is rotated against the Ti-C-N composite coated and uncoated AISI SS410. The worn surfaces were examined with scanning electron microscopy (SEM) (with EDAX attachment). The more grooving region, pits, ploughing ridge were found on the worn surface of the high carbon steel.
Authors and Affiliations
P. Vijayasarathi, P. Suresh Prabhu, Gukan Rajaram
Keywords
Related Articles
- EP ID EP50554
- DOI -
- Views 262
- Downloads 0
Adsorption of Reactive Blue 171 from aqueous solution using low cost activated carbon prepared from agricultural solid waste: Albizia amara
The adsorption of Reactive Blue 171 (Reactive Dye) from aqueous solution using activated carbon prepared from Albizia amara pod shell waste as an adsorbent have been carried out. The experimental adsorption data fitted r...
Thermo-physical properties measurment of water based Fe3O4 nanofluids
Two-step method was used to prepare nanofluids in which nanoparticles were first prepared and then dispersed in basefluid. This paper presents the effect of different volume fractions of magnetic Fe3O4 on thermal conduct...
Mechanical behavior of chemically treated Jute/Polymer composites
Fiber which serves as a reinforcement in reinforced plastics may be synthetic or natural past studies show that only artificial fibers such as glass, carbon etc., have been used in fiber reinforced plastics. Although gla...
Effect of temperature on the crystallite size of Lanthanum Cerium Oxide (La2Ce2O7) and its optical properties
The effect of the calcination process on the crystallite size and optical properties of Lanthanum Cerium Oxide (La2Ce2O7) nanopowders synthesized using co-precipitation process were reported. X-ray diffraction analysis r...
Experimental studies on improving the performance of electrochemical machining of high carbon, high chromium die steel using jet patterns
Electrochemical machining (ECM) is a non-traditional process used mainly to cut hard or difficult-to-cut metals, where the application of a more traditional process is not convenient. Stiff market competition and ever-gr...