3D Analyses of crack propagation in torsion
Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 33
Abstract
The initiation and propagation of fatigue cracks during cyclic torsion loading was studied in a cast Al alloy (A357) with a relatively large (~500 μm) grain size. 2D observations, revealed that multi site crack initiation occur on the {111} slip planes exhibiting the highest slip activity (iso-strain Taylor analysis), preferentially on planes nearly perpendicular to the sample axis. Within the first grain, the cracks have a pronounced crystallographic propagation mode (mode II crack growth) and strongly interact with the grain boundaries. In situ 3D monitoring of torsion fatigue tests using synchrotron X-ray tomography reveal that propagation towards the interior of the samples occurs first along the sample periphery in mode II leading to relatively shallow cracks which penetrate towards the sample center only after a large number of cycles is reached .The values of mode I, II and III stress intensity factors have been calculated from finite element simulation at the tip of the shallow mode II crack. Those values are used to analyse the bulk propagation of the observed cracks.
Authors and Affiliations
D. Shiozawa, I. Serrano-Munoz, S. Dancette, C. Verdu, J. Lachambre
Keywords
Related Articles
- EP ID EP89593
- DOI 10.3221/IGF-ESIS.33.07
- Views 94
- Downloads 0
A cohesive zone model to simulate the hydrogen embrittlement effect on a high-strength steel
The present work aims to model the fracture mechanical behavior of a high-strength low carbon steel, AISI 4130 operating in hydrogen contaminated environment. The study deals with the development of 2D finite...
Fracture mechanics of pseudoelastic NiTi alloys: review of the research activities carried out at University of Calabria
This paper reports a brief review of the research activities on fracture mechanics of nickel-titanium based shape memory alloys carried out at University of Calabria. In fact, this class of metallic alloys show a u...
Improvement of performance of ultra-high performance concrete based composite material added with nano materials
Ultra-high performance concrete (UHPC), a kind of composite material characterized by ultra high strength, high toughness and high durability. It has a wide application prospect in engineering practice. But t...
In-service fatigue cracking of the propeller shafts joined by a spline-pinned construction to the engines of AN-24, AN-26, and IL-18 aircrafts
The paper delivers a critical review of the research data on the crack initiation and crack growth patterns characteristic of the components of the spline-bolted joints between the propeller shaft and reducer sha...
Some practical crack path examples
It is well known that many engineering structures and components, as well as consumer items, contain cracks or crack-like flaws. It is widely recognised that crack growth must be considered both in design and in...