Critical crack path assessments in failure investigations
Journal Title: Frattura ed Integrità Strutturale - Year 2015, Vol 9, Issue 34
Abstract
This paper presents a case study in which identification of the controlling crack path was critical to identifying the root cause of the failure. The case involves the rupture of a 30-inch (0.76 m) natural gas pipeline in 2010 that tragically led to the destruction of a number of homes and the loss of life. The segment of the pipeline that ruptured was installed in 1956. The longitudinal seam of the segment that ruptured was supposed to have been fabricated by double submerged arc welding. Unfortunately, portions of the segment only received a single submerged arc weld on the outside, leaving unwelded areas on the inside diameter. Post-failure examination of the segment revealed that the rupture originated at one of these unwelded areas. Examination also revealed three additional crack paths or zones emanating from the unwelded area: a zone of ductile tearing, a zone of fatigue, and a zone of cleavage fracture, in that sequence. Initial investigators ignored the ductile tear, assumed the critical crack path was the fatigue component, and (incorrectly) concluded that the root cause of the incident was the failure of the operator to hydrotest the segment after it was installed in 1956. However, as discussed in this paper, the critical path or mechanism was the ductile tear. Furthermore, it was determined that the ductile tear was created during the hydrotest at installation by a mechanism known as pressure reversal. Thus the correct root cause of the rupture was the hydrotest the operator subjected the segment to at installation, helping to increase the awareness of operators and regulators about the potential problems associated with hydrotesting.
Authors and Affiliations
Robert Caligiuri
Keywords
Related Articles
- EP ID EP112015
- DOI 10.3221/IGF-ESIS.34.13
- Views 59
- Downloads 0
Are the Paris’ law parameters dependent on each other?
The question about the existence of a correlation between the parameters C and m of the Paris’ law is re-examined in this paper. According to dimensional analysis and incomplete self-similarity concepts applied to...
High-cycle fatigue strength of a pultruded composite material
Dealing with composites in polymeric matrix, the pultruded ones are among the more suitable for large production rates and volumes. For this reason, their use is increasing also in structural applications in civil and...
Critical crack path assessments in failure investigations
This paper presents a case study in which identification of the controlling crack path was critical to identifying the root cause of the failure. The case involves the rupture of a 30-inch (0.76 m) natural gas pip...
A simple beam model to analyse the durability of adhesively bondedtile floorings in presence of shrinkage
A simple beam model for the evaluation of tile debonding due to substrate shrinkage is presented.The tile-adhesive-substrate package is modeled as an Euler-Bernoulli beam laying on a two-layer elasticfoundation. An...
Effetto delle dimensioni del cordone di saldatura sulla resistenza a fatica dei giunti a croce
La scelta della dimensione da assegnare al cordone di saldatura nel caso di giunzioni saldate a croce può presentarsi problematica, specie quando gli spessori delle lamiere che formano il giunto sono differenti tra loro....