Abstract

Abstract-: This research presents new matrixes geo-polymer concrete, cementing mainly on engineering properties discusses the physical properties. In addition, the study of polymer concrete on two productions. GEO-polymer concrete GGBS and SF was created. Alkaline solution were used in this study. They are sodium hydroxide, sodium silicate solution and superplasticizer. 150 mm x 150 mm x 150 mm sample cube with a size of compressive strength were put to the test. GGBS concrete compressive strength of geo-polymer age 7, 14 and 28 days were 54.17, 66 and 69 on the MPa. And compressive strength of polymer concrete SF ground tests at the age of 7, 14 and 28 days were 1.45 1.42 1.45, and the MPa. GGBS concrete geo-polymer curing time at all compressive strength showed improved results. But geopolymer concrete compressive strength of SF given. In addition, 7 and 28 days old, low permeability and GGBS was made of geopolymer concrete were tested when absorption shown.