Preparation of iron doped carbon coated W18O49 and its photoactivity
Journal Title: Carbon - Science and Technology - Year 2008, Vol 1, Issue 1
Abstract
Iron doping to carbon coated W18O49 was carried out through solid-state reaction of WO2.9 with iron acetate at 400oC, followed by carbonization with poly(vinyl alcohol) (PVA) as carbon precursor at 800oC in N2 atmosphere. Photoactivities of these samples were confirmed by phenol photodecomposition in its aqueous solution. They revealed the photoactivity under visible light irradiation. Carbon coated W18O49 with iron exhibited higher photoactivity than it without iron. Addition of 1 % iron and 90/10 mixing ratio (WO2.9/PVA) derived the highest photoactivity to decompose the phenol.
Authors and Affiliations
Hany H. Abdel Ghafar, Tomoki Tsumura and Masahiro Toyoda
Keywords
Related Articles
- EP ID EP45924
- DOI -
- Views 422
- Downloads 0
Adsorption of Remazol Black B dye on activated carbon felt
The adsorption of Remazol Black B (anionic dye) on a microporous activated carbon felt is investigated from its aqueous solution. The surface chemistry of activated carbon is studied using X-ray microanalysis, "Boehm" t...
Mechanical Preparation, characterization and photocatalytic activity of Fe2O3/ZnO and Fe3O4/ZnO
Composite Iron oxide-Zinc oxide (α-Fe2O3/ZnO and Fe3O4/ZnO) was synthesized by two step method. In the first step, uniform α-Fe2O3 and Fe3O4 particles were prepared through a hydrolysis process of ferric chloride at 80 °...
Preparation of tailored carbons with meso- and micro- porosity via template synthesis route
A low cost templating approach to making non-ordered carbons with a tailored meso/micropore structure is described. A series of mesoporous carbons was prepared from polyfurfuryl alcohol and phenolic resin precursors by a...
Nutrient recovery and energy efficient algal harvest from anaerobic digestor wastewater
The increasing levels of generation of wastewaters which are nutrient rich pose serious issues where conventional biological and chemical methods of treatment have failed in meeting sustainability challenges. In this stu...
Effect of thermoplastic polyurethane content on properties of PC/TPU blend filled with Montmorillonite
The present study was taken up to investigate the effect of addition of Montmorillonite (MMT) to Poly carbonate/Thermoplastic polyurethane (PC/TPU) blends. A master batch of PC/MMT (70/30) was prepared using Hake Rheomix...